Zinc‑antimony binary system is an intermediate temperature thermoelectric material with great development prospects. In this work, Zn target and Sb target were jointed to form a composite target which was used for preparing ZINC ANTIMONIDE (cas 12039-35-9) thin films by ion beam sputtering deposition method. When the target was combined by Zn and Sb strips following 1/1 cycle, and the thin films were annealed at 275 °C, 300 °C, 325 °C, 350 °C and 375 °C separately, the main component of the films is ZnSb. The test results show that certain annealing temperature is conducive to the crystallization of the film. The maximum power factor of 0.4 Wm−1 K−2 was achieved at 275 °C when the thin film annealed at 375 °C. When the target was combined by Zn and Sb strips following 1/1/2/1 cycle, the film (T1) has main Zn4Sb3 phase and be rich in Zn. The composition of the film can be regulated by controlling the content of elements in the target.
We also recommend Trading Suppliers and Manufacturers of ZINC ANTIMONIDE (cas 12039-35-9). Pls Click Website Link as below: cas 12039-35-9 suppliers
About|Contact|Cas|Product Name|Molecular|Country|Encyclopedia
Message|New Cas|MSDS|Service|Advertisement|CAS DataBase|Article Data|Manufacturers | Chemical Catalog
©2008 LookChem.com,License: ICP
NO.:Zhejiang16009103
complaints:service@lookchem.com Desktop View