202667-44-5Relevant articles and documents
New catalyst system for producing polyethylene copolymers in a high temperature solution polymerization process
-
, (2015/11/09)
Catalyst system for producing ethylene copolymers in a high temperature solution process, the catalyst system comprising (i) a metallocene complex of formula (I) wherein M is Hf or Zr X is a sigma ligand L is a bridge of the formula -SiR72
ORGANOMETALLIC TRANSITION METAL COMPOUND, BISCYCLOPENTADIENYL LIGAND SYSTEM, CATALYST SYSTEM AND PREPARATION OF POLYOLEFINS
-
Page/Page column 39, (2010/02/12)
The present invention relates to organometallic transition metal compounds of the formula (I) where Mis an element of group 3, 4, 5 or 6 of the Periodic Table of the Elements or the lanthanides, the radicals X are identical or different and are each a
Control of stereoerror formation with high-activity "dual-side" zirconocene catalysts: A novel strategy to design the properties of thermoplastic elastic polypropenes
Dietrich, Ulf,Hackmann, Martijn,Rieger, Bernhard,Klinga, Martti,Leskelae, Markku
, p. 4348 - 4355 (2007/10/03)
The new C1-symmetric complexes rac-[1-(9-η5-fluorenyl)-2-(2-methylbenz[e]-1-η 5-indenyl)ethane]-zirconium dichloride (14a), rac-[1-(9-η5-fluorenyl)-2-(4,5-cyclohexa-2-methyl-1-η 5-indenyl)ethane]zirconium dichloride (14b), and rac-[1-(9-η5-fluorenyl)-2-(5,6-cyclopenta-2-methyl-l-η 5-indenyl)ethane]zirconium dichloride (15) were prepared in up to 93% yield. These compounds, activated with methyl aluminoxane, exhibit high active propene polymerization rates which remain constant over hours, even at elevated polymerization temperatures of 50 and 70°C. The two different coordination sites of these "dual-side" catalysts lead to isotactic polypropenes with variable amounts of stereoerrors, depending on the monomer concentration. The 2-methyl substituent of the indenyl ligands results, at the same time, in significantly increased molecular weights of the polymer products (up to 2.3 × 105 g mol-1), the bulk properties of which can be adjusted from flexible, semicrystalline thermoplastic to excellent thermoplastic elastic.