344762-21-6Relevant articles and documents
Regioselective synthesis, isomerisation, in vitro oestrogenic activity, and copolymerisation of bisguaiacol F (BGF) isomers
Koelewijn, Steven-Friso,Ruijten, Dieter,Trullemans, Laura,Renders, Tom,Van Puyvelde, Peter,Witters, Hilda,Sels, Bert F.
, p. 6622 - 6633 (2019)
Bisguaiacol F (BGF), a potentially safer and renewable bisphenol A (BPA) replacement made from lignin-derivable vanillyl alcohol (p-VA), is a promising building block for future aromatic biopolymers. Unfortunately, like BPA synthesis, this electrophilic condensation reaction is also prone to regioselectivity issues, giving rise to m,p′- and o,p′-BGF byproducts. In this work, the hitherto unconsidered influence of m,p′-BGF, viz. the main isomeric byproduct of p,p′-BGF synthesis, on the physicochemical properties of poly(BGF carbonate) (BGF-PC) was systematically investigated by random copolymerisation with different fractions of pure m,p′-BGF (25, 50 and 75 wt%). To do so, the elusive m,p′-isomer was made in unparalleled regioselectivity (72%) by alkylation condensation of isovanillyl alcohol (m-VA) with guaiacol. Surprisingly, no isomeric scrambling due to acid-catalysed isomerisation was encountered for pure BGF isomers, which strongly facilitates their synthesis in contrast to petrochemical bisphenol F (BPF). Furthermore, to ensure safer chemical design, an in vitro human oestrogen receptor α (hERα) transactivation assay was performed. Both pure m,p′- and p,p′-BGF displayed a significantly reduced oestrogenic potency (~426-457 times lower affinity than BPA) and oestrogenic efficacy (~39-50% of BPA's maximum induction). Interestingly, mutual comparison between p,p′-BPF and p,p′-BGF reveals and proves for the first time the direct link between ortho-methoxy substitution and reduced in vitro oestrogenic activity (for transactivation of hERα). In contrast to o,p′-BPA, viz. the main byproduct of p,p′-BPA synthesis, m,p′-BGF was proven suitable for utilization in thermoplastics, thereby avoiding time-consuming and labour-intensive (re)crystallizations to obtain regioisomerically pure p,p′-BGF.