High purity Rubber Accelerator ZBEC with best quality

Product Name:

Zinc dibenzyldithiocarbamate

Synonyms:

DIBENZYLDITHIOCARBAMIC ACID ZINC SALT;DIBENZYLDITHIOCARBAMIC ACID, ZN SALT;BENZYL ZIMATE;ZBDC;Zinc bis(N,N-dibenzyldithiocarbamate);ZINC DIBENZYLDITHIOCARBAMATE;ZINC N,N-DIBENZYLDITHIOCARBAMATE;bis[bis(phenylmethyl)carbamodithioato-S,S’]-,(T-4)-Zinc

CAS:

14726-36-4

MF:

C30H28N2S4Zn

MW:

610.21

Product Categories:

Organometallics;Classes of Metal Compounds;Transition Metal Compounds;Zn (Zinc) Compounds

Mol File:

14726-36-4.mol

Chemical Properties

melting point 

183-188 °C

boiling point 

408.3 °C at 760 mmHg

flashing point 

200.8 °C

vapor pressure 

7.06E-07 mmHg at 25°C

Item

Specifications

Power

dust suppressed Power

Granules

Appearance

White to light-cream Power( Granules)

Initial Melting Point, °C Min.

178

176

176

Heat Loss , % Max.

0.50

0.50

0.50

Zinc Content , %

10.0 - 11.5

9.8 - 11.3

10.0 - 11.5

Residue on ignition , % Max.

0.10

0.10

-

Zinc Salt Soluble in water, % Max.

0.05

0.05

0.05

Addtitive,%

-

1.0 - 2.0

0.5 - 1.5

Properties:

White to light-cream Power , relative density is 1.14g/cm3. melting point is above 178 ℃. Soluble in alchohol,benzene,chloromethane ,insoluble in water. Storage is stable.

Applications:

A overspead accelerator for natural and synthetic rubber and latex. Curing active temperature is low. It can substitute for ZDBC, ZDEC, PZ, ect .. Operating safety is much better. Specially , it will not produce cancer-causing nitrosamize during the rubber manufacturing process , and it can be used as excellent activator to kinds of thiazole . Appropriate matching quantity of Zine oxide and sulfur when using , and aliphatic acid is not necessary .it can be added directly into rubber mass and also can be added into latex as component part. ZBEC is regulated for use in articles in contact with food as specified under FDA 21 CFR 175.105,177.2600 and under BgVV XXI, Categories 1-4 and"Sonderkategorie ".

Storage:

Store closed containers in a cool, dry, well-ventilated area. Avoid exposure to direct sunlight.

Packing:

Coextruded paper bags lined with polyethylene film bags. Net weight 25 kg per bag.