CL937

Details:

Common name: CL937 scrape blade application wear resistant epoxy liquid rubber coating
(pasty fluid scrape coating rubber)

Category: Rubber liquid coating 

Appearance: Liquid

 

Brand Name: Colorcom

Shelf Life: 2 Years

Place of Origin: China 

 

Performance index:

Product Name	Physical state	Packaging	Viscosity （Pa•s） （25℃）	Operation time limit （25℃）	Curing time （25℃）
CL937 blade scrape application  wear resistant epoxy liquid rubber coating	fluid	25kg/group	Based on  users’ requirements	30 min	72 hours

 

Density (g/cm3)	Compressive  strength （Mpa）	Peeling strength （Mpa）	Hardness （shore A）	Breaking elongation （％）	Range of  temperature resistance （℃）
1.4	Based on  users’ requirements	Based on  users’ requirements	Based on  users’ requirements	Based on  users’ requirements	-60～80

 

 

Product Description:
Double components,black or red pasty fluid,with good thixotropy,not flowing,suitable for the blade coating construction on the surface of the equipment,generate the elastic rubber after curing,with strong bonding force to the substrates,high strength,water resistant,abrasion resistant,aging resistant.can be preparation of the elastomer of various hardness and mechanical performance index according to users’ requirements.Mainly used in the preparation of abrasion resistant rubber coating on the surface of various equipment,or do the thicken repairing on the surface of worn-out rubber layer.Such as the preparation of wear resistant rubber lining on the following equipment surface or do the surface repairing and regeneration: valve,pipeline,elbow,concentric reducer,roller of magnetic separator,flotation tank,chute,stock pan,hopper,bunker,mixing tank,shunt,conveyor belt,belt conveyor roller, fan shell and impeller,conditioning tower,powder selecting machine,thick powder separator, filter,cyclone tube,coal drop pipe,expansion joint,car compartment,garbage trucks cars, concrete tank car tanks,vibrating screen beam support,material storage tank etc.

 

Usage:

1.Surface treatment:Do the rust cleaning and coarsening processing on the pending-repair part,then clean it by cleaning agent or do the brush coating with special first coat based on users’ requirements.

2.For the workpiece which brushed coating or sprayed coating with first coat, you can’t do the next operation until the first coat curing

3.Configuration:Make the A and B two components mix uniformly according to the specified mass ratio.

4.scrape/blade coating:Make the mixed-up material scrape coating on the surface of the equipment uniformly

5.Curing: it can be put into using based on curing for 72 hours at room temperature.

 

Application: 

Scrape application anti wear liquid rubber epoxy coating
Package: Two-component,25Kg/group,packed in a plastic drum.

Storage: Sealed in dry, room temperature.

Executive Standards: International Standard.