CL935

Details:

Common name: CL935 spray application anti abrasion wear resistant epoxy compound liquid rubber coating

Category: Rubber liquid coating 

Appearance: Liquid

 

Brand Name: Colorcom

Shelf Life: 2 Years

Place of Origin: China 

 

Performance index:

Product Name	Physical state	Packaging	Viscosity （Pa•s） （25℃）	Operation  time limit （25℃）	Curing time （25℃）
CL935 spray application wear  resistant liquid rubber coating	fluid	25kg/group	Based on users’ requirements	30 min	72 hours

 

Density (g/cm3)	Compressive  strength （Mpa）	Peeling strength （Mpa）	Hardness （shore A）	Breaking  elongation （％）	Range of  temperature resistance （℃）
1.35	Based on  users’ requirements	Based on  users’ requirements	Based on  users’ requirements	Based on  users’ requirements	-60～80

 

Product Description:
Double components, black or red liquid,low viscosity,can add appropriate anhydrous solvent further diluted,suitable for the airless spraying(spray coating),generate the elastic rubber after curing,with strong bonding force to the substrates,high strength,water resistant,abrasion resistant,aging resistant.can be preparation of the elastomer of various hardness and mechanical performance index according to users’ requirements.Mainly used in the preparation of abrasion resistant rubber coating on the surface of various equipment,or do the thicken repairing on the surface of worn-out rubber layer.Such as the preparation of wear resistant rubber lining on the following equipment surface or do the surface repairing and regeneration: valve,pipeline,elbow,concentric reducer,roller of magnetic separator,flotation tank,chute,stock pan,hopper,bunker,mixing tank,shunt,conveyor belt,belt conveyor roller,fan shell and impeller,conditioning tower,powder selecting machine,thick powder separator, filter,cyclone tube,coal drop pipe,expansion joint,car compartment,garbage trucks cars, concrete tank car tanks,vibrating screen beam support,material storage tank etc.

 

Usage:

1.Surface treatment:Do the rust cleaning and coarsening processing on the pending-repair part,then clean it by cleaning agent or do the brush coating with special first coat based on users’ requirements.

2.For the workpiece which brushed coating or sprayed coating with first coat, you can’t do the next operation until the first coat curing

3.Configuration:Make the A and B two components mix uniformly according to the specified mass ratio.

4.Spray coating:Make the mixed-up material spray coating on the surface of the equipment with the airless sprayer.

5.Curing: it can be put into using based on curing for 72 hours at room temperature.

 

Application: 

Abrasion resistant spray application rubber liquid coating
Package: Two-component,25Kg/group,packed in a plastic drum.

Storage: Sealed in dry, room temperature.

Executive Standards: International Standard.