CL401

Details:

Common name: CL401 abrasion wearing resistant enamel repair putty epoxy compound

Category: Industrial repair agent

Appearance: Paste

 

Brand Name: Colorcom

Shelf Life: 2 Years

Place of Origin: China 

 

Performance index:

Product name	Physical state	Operation time limit (25℃)	Curing time (25℃)	Range of application
CL401 enamel epoxy repair putty compound	Paste	30 min	24 hours	Two components,used in the repairing and protecting of enamel reactor still enamel lining,can resist the erosion and erosive wear of acid (contain hydrofluoric acid),alkali and other materials effectively.

 

Color	Density (g/cm3)	Compressive strength (Mpa) GB1041-2008	Tensile strength (Mpa) GB6329-1999	Shear strength (Mpa) GB7124-2009	Bending strength (Mpa) GB1042-2008	Hardness after curing （Shore D） ASTM-D-2556	Liquid suggested using temperature (℃）
Gray	2.0	98	36	14	42	82	-60-80

 

Product Description:
CL401 wear abrasion resistant enamel epoxy repair ceramic putty compound is the high performance wear resistant,corrosion resistant polymeric material which compounded by the ultra-fine ceramic powder and modified toughening heat resistant resin.Specially used in the damaged repairing and protecting of enamel reactor still lining,can resist the erosion and erosive wear of acid (contain hydrofluoric acid),alkali and other materials.

 

Usage:

1.Surface treatment: Do the coarsening treatment on the pending-repair part,grinding with angle grinder or sand blasting etc,the surface after coarsening treatment should be cleaned,the surface after this treatment should be the one coarsening,dry and fresh substrates,should be no greasy dirt and dust.
 
2..Preparation:According to weight ratio or volume ratio A:B=4:1, make A and B two components mix uniformly,and use it up within 30 min.If the temperature is too low,can properly heat up the A component to reduce viscosity for easy to configure.
 
3.Coating:The suitable coating thickness of CL401 enamel repair putty epoxy compound  is 1-3mm.Make the well mixed material be coating on the pending-repair area layer by layer,the first layer should be compacted,make it infiltrate fully with the substrates.Repair the surface to be smooth after the coating spreading in the suitable size.
 
4.Curing:It can be put into using after curing for 24 hours at the temperature of 25 degree,(If you can heat it up to the temperature of 80 degree and keep this temperature for 2 hours,in this way,can improve 30% comprehensive performance) If the temperature is below 10 degree,should heat it up or prolong curing time to promote the curing.(General construction in winter,can inject the steam into the clamp cover or heat the conduction oil up to the temperature of 80 degree and heat preservation for curing)

 

Application: 

Two components,used in the repairing and protecting of enamel reactor still enamel lining,can resist the erosion and erosive wear of acid (contain hydrofluoric acid),alkali and other materials effectively.
Package: Two-component,25Kg/group,packed in a plastic drum.

Storage: Sealed in dry, room temperature.

Executive Standards: International Standard.