CL218

Details:

Common name: CL218 chemical abrasion wear resistant repair agent epoxy ceramic coating

Category: Industrial repair agent

Appearance: Paste

 

Brand Name: Colorcom

Shelf Life: 2 Years

Place of Origin: China 

 

Performance index:

product name	physical state	standard packaging	Volume (cm3)	operational time limit (25℃)	Time can be put into use (25℃)
CL218 wear chemical  resistant repair agent  epoxy coatings	paste	500g/set Two-components)	240	45min	24h

 

color	density (g/cm3)	compressive strength (Mpa) GB1041-2008	tensile strength (Mpa) GB6329-2008	shear strength (Mpa) GB7124-2008	bending strength (Mpa) GB1042-1999	working temperature （℃）
gray	2.43	115	39	23	54	-60～160

 

Product Description:
CL218 chemical wear resistant repairing agent epoxy ceramic coating is the high performance wear&corrosion resistant 
polymerization ceramic material compounded by high performance wear&corrosion resistant material (such as:ceramic,silicon carbide, silicon carbide, titanium alloy)  and modified toughening heat resistant resin.It’s widely used in repairing and pre-protecting of high duty coarse particles erosive wear of the pump body,fan shell, pipeline screw conveyor and so on.
 

Usage:

1.Surface treatment: Do coarsening treatment on the pending-repair area, grinding with angle grinder or sand blasting and so on, the surface after coarsening treatment should be cleaned,
the surface after this treatment should be the one coarsening,dry and fresh substrates,should be no greasy dirt and dust.
 
2.Preparation:According to weight ratio 8:1 or volume ratio 4:1, make A and B two components mix uniformly,and use it up within 30 min. According to the actual temperature,configuration can be appropriately a little more in winter,proper less in summer.If the temperature is too low,you can properly heat up the A component to reduce viscosity for easy to configure.
 
3.Coating: The suitable coating thickness of CL218 anti wear abrasion epoxy ceramic coating repair agent is 4-8mm. Make mixed-up material spread coating on the pending-repair area layer by layer, the first layer should be compacted,make it infiltrate fully with the substrates.Repair the surface to be smooth after the coating spreading in the suitable size or use CL406 corrosion resistant repairing agent to coat on the surface of the coating, this material can’t do machining,so you should pay attention to controlling the coating thickness to avoid appearing interference phenomenon in the assembly.
 
4.Curing: Cure for 24 hours at the temperature of 25 degree before using. If the temperature is low,should heat it up or prolong curing time to promote the curing.
General construction in winter,you can use iodine tungsten lamp do irradiation heating with 40cm distance from the coating.

 

Application: 

Chemical wear resistant repair agent ceramic coating
Package: Two-component,25Kg/group,packed in a plastic drum.

Storage: Sealed in dry, room temperature.

Executive Standards: International Standard.