The SIBELIUS experiment was designed to obtain information on the compatibility between beryllium and ceramics, as well as beryllium and steel, in a neutron environment. This experiment comprised irradiation of eight capsules, seven of which were independently purged with a He/0.1% H2 gas mixture. Four capsules were used to examine beryllium/ceramic (Li2O, LiAlO2, Li4SiO4, and Li2ZrO3) and beryllium/steel (Types 316L and 1.4914) compacts. Isothermal anneal experiments have been run on representative beryllium and ceramic disks from each of the four capsules at 550 to 850°C in steps of 100°C. The results indicate that tritium release from the beryllium did not exhibit burst release behavior, as previously reported, but rather a progressive release with increasing temperature. Generally, ∼99% of the tritium was released by 850°C. Tritium release from the ceramic discs was quite similar to the behavior shown in other dynamic tritium release experiments on lithium ceramics. The tritium content in beryllium discs adjacent to a steel sample was found to be significantly lower than that found in a beryllium disc adjacent to a ceramic sample. Recoil of tritium from the ceramic into the beryllium appears to be the source of tritium entering the beryllium, probably residing in the beryllium oxide layer.
We also recommend Trading Suppliers and Manufacturers of Beryllium aluminate. (cas 12004-06-7). Pls Click Website Link as below: cas 12004-06-7 suppliers
About|Contact|Cas|Product Name|Molecular|Country|Encyclopedia
Message|New Cas|MSDS|Service|Advertisement|CAS DataBase|Article Data|Manufacturers | Chemical Catalog
©2008 LookChem.com,License: ICP
NO.:Zhejiang16009103
complaints:service@lookchem.com Desktop View