Ca-α-SiAlON powder was prepared by carbothermal reduction nitridation process at nitrogen atmosphere without using high pressure and long holding time. The precursor was prepared by a novel colloidal sol-gel process consisting of silica, alumina, calcium oxide and carbon. The obtained powders were characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), and scanning electron microscopy (SEM). The XRD and SEM analysis results revealed that by heating at 1200 °C for 2 h, spherical particles consisting of amorphous calcium aluminosilicate liquid phase were formed. With increasing temperature to 1360 °C and held for 2 h, the spherical particles with the dominant phase of O–SiAlON were observed. Finally, as the temperature climbed to 1500 °C and held for 2 h, spherical particles disappeared and Ca-α-SiAlON was formed. The XRD analysis of the products showed that with increasing temperature from 1360 °C to 1500 °C, O–SiAlON, β-SiAlON and Ca-α-SiAlON were formed, respectively, and colloidal sol-gel method, due to the high homogeneity of the reactants, had a significant role in increasing the purity of Ca-α-SiAlON.
We also recommend Trading Suppliers and Manufacturers of SIALON (cas 112760-32-4). Pls Click Website Link as below: cas 112760-32-4 suppliers
About|Contact|Cas|Product Name|Molecular|Country|Encyclopedia
Message|New Cas|MSDS|Service|Advertisement|CAS DataBase|Article Data|Manufacturers | Chemical Catalog
©2008 LookChem.com,License: ICP
NO.:Zhejiang16009103
complaints:service@lookchem.com Desktop View