A biodegradable film based on gelatin extracted from chrome leather scrap was studied in this paper. According to the results of a variety of characterization, the extracted gelatin contains 13 kinds of amino acid; the chrome content is 30 mg/kg, mineral and salt content are both at low levels and the nitrogen content is 43.84%. Its molecular weight has been measured at about 6.5 kDa ∼26.6 kDa, and the average particle distribution appears to be 125 nm with a narrow distribution. When the extracted gelatin was modified with the β-cyclodextrin to prepare the biodegradable films, the β-cyclodextrin and gelatin blends can build up perfect compatibility and film-forming properties. Comparing to the gelatin film without β-cyclodextrin, the viscosity, biodegradability, thermal stability and physical properties of the β-cyclodextrin and gelatin blends in the present research were significantly increased, especially when the ratio of β-cyclodextrin to gelatin was 1:2, the biodegradation rates reached 81%, elongation at break 15.74% and the tensile strength 122.34 MPa. The blends show perfect swelling properties and overcome the rapid solubility drawback of extracted gelatin.
We also recommend Trading Suppliers and Manufacturers of Chromic acetate (cas 1066-30-4). Pls Click Website Link as below: cas 1066-30-4 suppliers
About|Contact|Cas|Product Name|Molecular|Country|Encyclopedia
Message|New Cas|MSDS|Service|Advertisement|CAS DataBase|Article Data|Manufacturers | Chemical Catalog
©2008 LookChem.com,License: ICP
NO.:Zhejiang16009103
complaints:service@lookchem.com Desktop View