The atomic layer deposition (ALD) of TiO2 from tetrakis(dimethylamino)titanium (TDMAT) and water was studied in the substrate temperature (TS) range of 120 °C to 330 °C.The effect of deposition temperatures on the resulting layer microstructure is investigated. Based on the experimental results, possible interaction mechanisms of TDMAT and H2O precursor molecules and the TiO2 surface at different temperatures are discussed. The TiO2 layers were characterized with respect to microstructure, composition and optical properties by glancing angle x-ray diffraction and reflectometry, x-ray fluorescence analysis, photoelectron spectroscopy and spectroscopic ellipsometry. A constant layer growth with increasing number of ALD cycles was achieved for all investigated deposition temperatures, if the inert gas purge time after the H2O pulse was increased from 5 s at temperatures below 250 °C to 25 s for TS ≥ 320 °C. In the investigated temperature range, the growth per cycle varies between 0.33 and 0.67 Å/cycle with a minimum at 250 °C.The variations of the deposition rate are related to a change from a surface determined decomposition of TDMAT to a gas phase decomposition route above 250 °C. At the same temperature, the microstructure of the TiO2 layers changes from amorphous to predominately crystalline, where both anatase and rutile are present.
We also recommend Trading Suppliers and Manufacturers of TETRAKIS(DIMETHYLAMINO)TIN (cas 1066-77-9). Pls Click Website Link as below: cas 1066-77-9 suppliers
About|Contact|Cas|Product Name|Molecular|Country|Encyclopedia
Message|New Cas|MSDS|Service|Advertisement|CAS DataBase|Article Data|Manufacturers | Chemical Catalog
©2008 LookChem.com,License: ICP
NO.:Zhejiang16009103
complaints:service@lookchem.com Desktop View