In order to effectively polish the surface of the titanium alloy workpiece, a novel type of iron nitride magnetic abrasives was designed, prepared and characterized. Theoretically, first-principles were used to analyze the effects of phase compositions of iron nitrogen compounds on the mechanical and magnetic properties of the abrasive, and ε-Fe3N and γ′-Fe4N were determined as the grinding phase compositions with the simultaneously improved properties of hardness, ductility and magnetism. In the experiments, the core-shell structured iron nitrogen compounds were prepared by nitriding the iron powders of about 250 μm with ammonia at 600 °C, and the effects of nitriding time, ammonia pressure and cooling method on the product were investigated. The composition, morphology, magnetic properties and mechanical properties of the product were characterized by X-ray diffraction (XRD), scanning electron microscope (SEM), magnetometer and nanoindenter, respectively. Under experimental conditions of ammonia pressure of 0.2 Mpa, nitriding time of 3 h and water quenching, the abrasive was obtained with the external grinding phase of ε-Fe3N and γ′-Fe4N in a thickness of 35.10 μm and the internal ferromagnetic phase of α-Fe. Its magnetic saturation intensity and hardness were 148.5 A m2 kg−1 and 8.15 GPa, respectively. Grinding with this abrasive, the surface roughness of Ti–6Al–4V alloy plate was effectively reduced from 0.305 μm to 0.077 μm.

We also recommend Trading Suppliers and Manufacturers of iron, compound with titanium (2:1) (cas 12023-40-4). Pls Click Website Link as below: cas 12023-40-4 suppliers