Spark plasma sintering (SPS) experiments were conducted to investigate the effect of the processing parameters such as temperature, mechanical pressure and dwell time on densification behavior of monolithic CHROMIUM DIBORIDE (cas 12007-16-8). The sintering experiments were performed at different temperatures ranging from 1100 °C to 1900 °C under the mechanical pressure of 30 MPa–70 MPa for 1 min–15 min duration. The onset temperature for the densification of CrB2 is observed to be 1300 °C at 50 MPa. High dense chromium diboride (98.4%ρth) compact was obtained when processed at 1900 °C under a mechanical pressure of 70 MPa for 15 min duration. Hardness and fracture toughness of high density monolithic CrB2 (98.4%ρth) sample were measured to be 15.89 ± 1.3 GPa and 1.8 ± 0.14 MPa·m1/2 respectively.
We also recommend Trading Suppliers and Manufacturers of CHROMIUM DIBORIDE (cas 12007-16-8). Pls Click Website Link as below: cas 12007-16-8 suppliers
About|Contact|Cas|Product Name|Molecular|Country|Encyclopedia
Message|New Cas|MSDS|Service|Advertisement|CAS DataBase|Article Data|Manufacturers | Chemical Catalog
©2008 LookChem.com,License: ICP
NO.:Zhejiang16009103
complaints:service@lookchem.com Desktop View