Experimental investigations were carried out on synthesis of chromium diboride through boron carbide reduction of Cr2O3. The products obtained were characterized by X-ray diffraction and the process optimized to prepare single-phase CrB2 powder. Densification of CrB2 was investigated by pressureless sintering and hot pressing. A maximum of 93% ρth was obtained by pressureless sintering at 1850 °C after a prolonged duration of 360 min. However, near theoretical density was achieved by hot pressing at 1600 °C and 35 MPa pressure for 2 h. The hardness and fracture toughness of fully dense CrB2 was measured as 22 GPa and 3.5 MPa m1/2, respectively. The mode of fracture in pressureless sintered samples is intergranular whereas that in hot pressed is transgranular.
We also recommend Trading Suppliers and Manufacturers of CHROMIUM DIBORIDE (cas 12007-16-8). Pls Click Website Link as below: cas 12007-16-8 suppliers
About|Contact|Cas|Product Name|Molecular|Country|Encyclopedia
Message|New Cas|MSDS|Service|Advertisement|CAS DataBase|Article Data|Manufacturers | Chemical Catalog
©2008 LookChem.com,License: ICP
NO.:Zhejiang16009103
complaints:service@lookchem.com Desktop View