magnesium borate (cas 12007-62-4) fibers were prepared by electrospinning technique (and following calcination) from sol–gel precursors, using polyvinyl-pyrrolidone (PVP) as processing aid. Phase-pure fibers of about 6 μm in diameter were obtained by high temperature calcination of the inorganic–organic composite mats. The samples thus prepared were characterized by means of SEM, XRD and FT-IR, respectively. The concentration of the initial solution influenced only the fiber diameter in the green samples, while the final dimension after ceramization was related to the formation of new porous fibers in a preferential direction. This phenomenon resulted from some orientation already present in the green mats, and from the softening and densification of the fibers after decomposition of the PVP. An incomplete crystallization of the samples was observed after heat treatment at 800 °C, with a residual glassy phase due to the Mg modification of the B2O3 network. Fully crystalline fibers were obtained from the mats calcined at 1000 °C.
We also recommend Trading Suppliers and Manufacturers of magnesium borate (cas 12007-62-4). Pls Click Website Link as below: cas 12007-62-4 suppliers
About|Contact|Cas|Product Name|Molecular|Country|Encyclopedia
Message|New Cas|MSDS|Service|Advertisement|CAS DataBase|Article Data|Manufacturers | Chemical Catalog
©2008 LookChem.com,License: ICP
NO.:Zhejiang16009103
complaints:service@lookchem.com Desktop View