In this study, a 2.7 wt% (Fe)/97.3 wt% (Zn0.3Ni0.7Fe2O4) nanocomposite (45–100 nm) was synthesized uisng the non-alkoxide complex sol-gel method by controlling the amount of Triethanolamine (TEA) and the annealing temperature. Various instuments including the simultaneous thermal analyzer (STA), Fourier transform infrared spectrometer, X-ray diffraction, scanning electron microscope equipped with X-ray dispersive spectroscopy, and vibrating sample magnetometer were used to characterize the samples. The STA results showed that the gel was converted from the amorphous phase to a crystalline one at 750 °C. The XRD pattern at the temperature of 750 °C also confirmed the presence of a spinel ferrite structure, α- Fe2O3 and Fe phases. By increasing the annealing temperature to 1100 °C, α- Fe2O3 as an impurity phase was eliminated, but the iron phase (formed through the reduction of the partial Fe3+ ions by TEA molecules as a sacrificial reducing agent) was still present. According to the VSM analysis of the SPSed sample, the exchange coupling between the iron phase and nickel zinc ferrite nanoparticles significantly improved the saturation magnetization of the spinel ferrite from 66.0 emu/g to 82.9 emu/g.
We also recommend Trading Suppliers and Manufacturers of Nickel zinc ferrite (cas 106389-78-0). Pls Click Website Link as below: cas 106389-78-0 suppliers
About|Contact|Cas|Product Name|Molecular|Country|Encyclopedia
Message|New Cas|MSDS|Service|Advertisement|CAS DataBase|Article Data|Manufacturers | Chemical Catalog
©2008 LookChem.com,License: ICP
NO.:Zhejiang16009103
complaints:service@lookchem.com Desktop View