Silicon nitride-based composite ceramics with different contents of MAGNESIUM TITANATE (cas 12032-30-3) have been fabricated via gas pressure sintering method. The phase compositions, microstructure, mechanical performances and dielectric properties of the composite ceramics were investigated. The density of the Si3N4-based composite ceramics firstly increased with additive of magnesium titanate powder up to 5 wt% and then gently decreased, and the mechanical properties firstly increased and then declined. Besides, the dielectric constant and dielectric loss increased with the increase of magnesium titanate contents. For the Si3N4-based composite ceramics with 5 wt% magnesium titanate powders, the flexural strength, elastic modulus, dielectric constant and dielectric loss reached 451 MPa, 274 GPa, 7.65, 0.0056, respectively. These results suggested that the magnesium titanate was beneficial for the improvement of mechanical performances and dielectric constant of Si3N4-based composite ceramics.
We also recommend Trading Suppliers and Manufacturers of MAGNESIUM TITANATE (cas 12032-30-3). Pls Click Website Link as below: cas 12032-30-3 suppliers
About|Contact|Cas|Product Name|Molecular|Country|Encyclopedia
Message|New Cas|MSDS|Service|Advertisement|CAS DataBase|Article Data|Manufacturers | Chemical Catalog
©2008 LookChem.com,License: ICP
NO.:Zhejiang16009103
complaints:service@lookchem.com Desktop View