Add time:07/30/2019 Source:sciencedirect.com
Due to the health concerns, the demand for Pb-free solder is greater than before. In the past, Sn-Pb solders were widely used in soldering process due to their excellent soldering characteristics and reliability. Pb-free solder, the Sn-8Zn-3Bi eutectic alloy is regarded as one of the best potential candidates. This study investigated the effect of silver (Ag) addition on the morphology and growth rate of Cu5Zn8, Cu6Sn5 and Cu3Sn intermetallics in the Sn-8Zn-3Bi solder. The reflow was done at 220°C, 230°C, 250°C, 270°C and 290°C at various soldering times. The Sn-8Zn-3Bi solder reacting with Cu substrate formed a single Cu5Zn8 intermetallic layer with a flat structure. On the other hand, the reaction between (Sn-8Zn-3Bi)-1Ag solder and Cu substrate produces Cu6Sn5 and Cu3Sn intermetallics. The addition of Ag into the Sn-8Zn-3Bi solder has significantly suppressed the formation of Cu5Zn8 intermetallic, and promoted the growth of Cu6Sn5 and Cu3Sn intermetallics. The growth rate constants of Cu5Zn8 phase is lower at low temperature and increases at high temperature. Meanwhile the growth rate constants of Cu6Sn5 is higher than Cu3Sn phase, thus providing an opportunity for Cu6Sn5 phase to predominate the total intermetallic compounds in this liquid-state aging study.
We also recommend Trading Suppliers and Manufacturers of Silver, compd. with zinc (1:1) (cas 12041-17-7). Pls Click Website Link as below: cas 12041-17-7 suppliers
About|Contact|Cas|Product Name|Molecular|Country|Encyclopedia
Message|New Cas|MSDS|Service|Advertisement|CAS DataBase|Article Data|Manufacturers | Chemical Catalog
©2008 LookChem.com,License: ICP
NO.:Zhejiang16009103
complaints:service@lookchem.com Desktop View