A new way to improve the 1.53 μm emission in Er3+/Yb3+ co-doped multicomponent phosphate glass was demonstrated by introducing silver nanoparticles (NPs) in rare-earth doped glass. The existence of Ag NPs was confirmed by absorption spectra and transmission electron microscopy (TEM) measurements. The homogeneous distribution of silver NPs could be observed by the TEM images. UV-Vis-NIR absorption spectra revealed that the surface plasmon band was centered at about 420 nm. The photoluminescence spectra of glass samples were used to investigate the effect of silver NPs on the fluorescence properties of Er3+. Efficient 1.53 μm emission was obtained in prepared samples when pumped at 980 nm laser diode (LD). The 1.53 μm emission intensity could be enhanced 87% by doping 2 mol.% AgCl due to the increased localized field effect in the vicinity of NPs and the possible energy transfer from silver NPs to Er3+ ions. Our present work may point out one way to enhance the gain coefficient of Er3+/Yb3+ co-doped glass fiber.
We also recommend Trading Suppliers and Manufacturers of Silver, compd. with zinc (1:1) (cas 12041-17-7). Pls Click Website Link as below: cas 12041-17-7 suppliers
About|Contact|Cas|Product Name|Molecular|Country|Encyclopedia
Message|New Cas|MSDS|Service|Advertisement|CAS DataBase|Article Data|Manufacturers | Chemical Catalog
©2008 LookChem.com,License: ICP
NO.:Zhejiang16009103
complaints:service@lookchem.com Desktop View