Polycrystalline samples of AxV2Al20 (A = Ce, Th, U, Np, Pu; 0.7 ≤ x ≤ 1.0) actinide intermetallics were synthesized using the arc-melting method. Crystal structure studies were performed by means of powder x-ray diffraction and the Rietveld refinement method. All studied compounds crystallize in the CeCr2Al20-type structure (space group Fd-3m, no. 227) with the actinide or Ce atom located in the oversized cage formed by Al atoms. Comparison of the crystallographic results with the reported data for LnV2Al20 (Ln = lanthanides) counterparts reveals distinctly different behavior of the lanthanide- and actinide-bearing compounds. This difference is suggested to be caused by fairly localized character of the 4f electrons, whereas itinerant character of the 5f electrons is likely seen for U- and Np-containing phases. Magnetic susceptibility and specific heat measurements did not reveal any magnetic ordering in U0.8V2Al20, Np0.8V2Al20 and Pu0.8V2Al20 down to 2.5 K. A small anomaly in low-temperature specific heat of Ce0.8V2Al20, U0.8V2Al20, and Np0.8V2Al20 is observed, likely arising from a low-energy Einstein mode.

We also recommend Trading Suppliers and Manufacturers of THORIUM ALUMINIDE (cas 12043-43-5). Pls Click Website Link as below: cas 12043-43-5 suppliers