Simultaneous synthesis and densification of Boron carbide (cas 12069-32-8) and boron carbide- graphene nano platelets (GNP) were carried out by reactive spark plasma sintering of amorphous boron and graphene nano platelets at temperature ranging from 1200 to 1600 °C, pressure of 50 MPa and heating rate of 50 °C/min and 100 °C/min. X-ray diffraction and Raman spectroscopy confirmed the formation of required phases. Electron microscopic images revealed the formation of sub-micron and nano sized grains of plate like morphology. Sintered product with high relative density of 96%TD was achieved at a temperature of 1600 °C and heating rate of 50 °C/min for B4C stoichiometric composition and also exhibited maximum hardness of 21.10 GPa.
We also recommend Trading Suppliers and Manufacturers of Boron carbide (cas 12069-32-8). Pls Click Website Link as below: cas 12069-32-8 suppliers
About|Contact|Cas|Product Name|Molecular|Country|Encyclopedia
Message|New Cas|MSDS|Service|Advertisement|CAS DataBase|Article Data|Manufacturers | Chemical Catalog
©2008 LookChem.com,License: ICP
NO.:Zhejiang16009103
complaints:service@lookchem.com Desktop View