The YTTRIUM NITRATE (cas 10361-93-0) effect on FeSiCr alloy insulating layer thickness and magnetic properties after annealing treatment is investigated in this study. The results showed that a continuous chromium oxide layer was observed on the FeSiCr alloy powder surface after annealing at 800 °C. The addition of a minor amount of yttrium nitrate can significantly slow the FeSiCr alloy powder oxidation rate. However, excessive yttrium nitrate addition accelerated the oxide layer growth. The FeSiCr alloy sample magnetic properties depend strongly on the chromium oxide layer thickness. The saturation magnetization and initial permeability increased with increasing yttrium nitrate and reached the maximum at 0.02 wt% and then decreased as the addition amount was increased to 0.5 wt%. The addition of 0.02 wt% yttrium nitrate into FeSiCr alloy powder can effectively improve the saturation magnetization, initial permeability, quality factor and magnetic loss, which provides a promising candidate for power chip inductor applications.
We also recommend Trading Suppliers and Manufacturers of YTTRIUM NITRATE (cas 10361-93-0). Pls Click Website Link as below: cas 10361-93-0 suppliers
About|Contact|Cas|Product Name|Molecular|Country|Encyclopedia
Message|New Cas|MSDS|Service|Advertisement|CAS DataBase|Article Data|Manufacturers | Chemical Catalog
©2008 LookChem.com,License: ICP
NO.:Zhejiang16009103
complaints:service@lookchem.com Desktop View