Copper and iron SBA-16 catalysts were synthesized using hydrothermal method and modified with potassium. XRD patterns showed that characteristic peaks of SBA-16 for all catalysts did not destroy with metal loading. The metal and potassium loading to SBA-16 structure led to generally the decreasing of specific surface area values. While total pore volume value of SBA-16 increased with copper loading, it decreased with iron loading. Pore diameter values of SBA-16 generally increased with metal loading. It was seen that from TEM images metals settled as nanoparticles to the SBA-16 structure. EDX results demonstrated that potassium modification treatment increased especially the success of metal loading. FTIR spectrums of all catalysts exhibited the characteristic structural bands of SBA-16. It was seen that the peak intensity of both Brønsted and Brønsted + Lewis acid sites of the SBA-16 increased by the metal loading. On the other hand potassium modification improved the acid sites. UV–Vis DR and XPS spectra showed that copper and iron species settled as Cu+2 and Fe+3 form, respectively. The potassium modified catalysts exhibited the highest conversion of 77% and acetaldehyde selectivity of 81% compared to catalysts without potassium modification at reaction temperature of 350 °C.
We also recommend Trading Suppliers and Manufacturers of iron potassium oxide (cas 12160-30-4). Pls Click Website Link as below: cas 12160-30-4 suppliers
About|Contact|Cas|Product Name|Molecular|Country|Encyclopedia
Message|New Cas|MSDS|Service|Advertisement|CAS DataBase|Article Data|Manufacturers | Chemical Catalog
©2008 LookChem.com,License: ICP
NO.:Zhejiang16009103
complaints:service@lookchem.com Desktop View