In this study, mesoporous carbonated TiO2 nanoparticles were synthesized by sol-gel route using a complex [Ti(OH2)6]3+·3Cl− and a modifying agent Na2CO3 and used as an adsorbents for Sr(II) removal from aqueous medium. The characterization of nanoadsorbents was accomplished using XRD, SEM, EDS, TEM, TG-DTG-DTA, IR, BET, pHPZC analyses. It was found that the sizes of carbonated TiO2 nanoparticles was ~4 nm. The presence of mononuclear bidentate carbonate groups on the titania surface was approved by IR spectroscopy. The kinetic data was analyzed by pseudo-first-order, pseudo-second-order, Elovich, and an intraparticle diffusion models. The adsorption isotherms were fitted by using Langmuir, Freundlich, and Dubinin–Radushkevich models. The fittings show that the pseudo-second-order kinetics and Langmuir isotherm are suitable models for the adsorption process. The sample with 4% (wt.) of carbonate groups showed the best adsorption performance towards Sr(II) cations. The mesoporous carbonated samples demonstrated a higher adsorption capacity for strontium ions than the basic TiO2. The adsorption capacities of modified 2C-TiO2, 4C-TiO2 and 8C-TiO2 samples were 170.4, 204.4, 190.8 mg/g respectively, while it was 70.9 mg/g for the unmodified TiO2 towards Sr(II). Higher removal of Sr(II) was observed in the alkaline medium due to the formation of SrОН+ cations. A mechanism for Sr(II) adsorption was described and the number of chemosorbed ≡Ті(О2СО) groups and active adsorption centers onto unmodified and modified TiO2 surface were calculated. The titania adsorbents have high reusability and retain their adsorption capacity during five adsorption-desorption cycles. The presented results indicated that the mesoporous carbonated adsorbents were appropriate materials for the removal of Sr(II) from aqueous medium.

We also recommend Trading Suppliers and Manufacturers of STRONTIUM ARSENATE (cas 13464-68-1). Pls Click Website Link as below: cas 13464-68-1 suppliers