Phase composition and phase transitions, spectral characteristics, thermal and transport properties of the (1-x)RbH2PO4 – xRb2HPO4 · yH2O system at the wide range of х = 0–1 were investigated. No solid solutions were observed at the system. A monophasic region at х = 0.25 with the compound Rb5H7(PO4)4 was found. The thermodynamic and transport properties of Rb5H7(PO4)4 were studied in detail. The other compositions correspond to diphasic mixtures of two salts: RbH2PO4 and Rb5H7(PO4)4 (х = 0–0.2), or Rb2HPO4·yH2O and Rb5H7(PO4)4 (at х higher 0.25). The sharp increase of proton conductivity up to 3·10−2 S/cm under highly humidified conditions was found for х = 0.1–0.25 at temperatures >240 °С can be associated with the superionic phase transitions of RbH2PO4 and Rb5H7(PO4)4. A weak composite effect with a slight increase of conductivity (about one order of magnitude) at low temperatures compared to those for the pure salts RbH2PO4 and Rb2HPO4·2H2O was shown for all samples.

We also recommend Trading Suppliers and Manufacturers of Sodium dihydrogen phosphate dihydrate (cas 13472-35-0). Pls Click Website Link as below: cas 13472-35-0 suppliers