ZrB2-SiC-Cr powder sintering at 1600 °C and its oxidation behavior at 1000–1500 °C in air were studied as a function of chromium content. It was shown that the relative density of the ZrB2-SiC ceramics increases with an increase in chromium content in the powdered mixture. This is related to the formation of the liquid Cr-Si-C-B phase during the high-temperature interaction of SiC with chromium and ZrB2.It was stated that the mechanism of ZrB2-SiC-Cr ceramics oxidation is changed from bulk to passive. The oxidation resistance is improved for the ceramics with 13% of chromium or less, which can be explained by a decrease in its porosity. The ceramics with higher chromium content demonstrates the opposite effect, namely, large-size Cr2O3 crystals are formed during oxidation, this promotes microcracking in the oxidizing layer and causes damage of surface integrity. As a result, the oxidation resistance of the ZrB2-SiC-Cr ceramics with high chromium content is decreased.
We also recommend Trading Suppliers and Manufacturers of Chromium oxide (cas 1308-38-9). Pls Click Website Link as below: cas 1308-38-9 suppliers
About|Contact|Cas|Product Name|Molecular|Country|Encyclopedia
Message|New Cas|MSDS|Service|Advertisement|CAS DataBase|Article Data|Manufacturers | Chemical Catalog
©2008 LookChem.com,License: ICP
NO.:Zhejiang16009103
complaints:service@lookchem.com Desktop View