Carbon materials of boron content ranging from 0.6 to 4 wt.% were synthesized by co-pyrolysis of QI-free coal–tar pitch with the borane–pyridine complex. The growing amount of boron introduced into the carbonaceous material is associated with an increase in nitrogen content and a progressive degradation of structural and textural ordering. The structural variations of the boron-doped materials on heat treatment up to 2500 °C were monitored using X-ray diffraction and X-ray photoelectron spectroscopy. The intrinsic boron acts effectively as a catalyst of graphitization above 2100 °C. The carbonaceous material with boron content of about 1.5 wt% shows the highest degree of structural ordering after thermal treatment. A high amount of oxygen was found in the graphitized boronated carbons, proving that the incorporated boron induces a strong chemisorption activity of the material when exposed to air. For a series of cokes calcined at 1000 °C, the most striking effect of increasing the boron content is an increase of irreversible capacity Xirr from 0.2 to 0.7. The reversible capacity (Xrev) amounts to about 1, with a slight tendency to decrease with the boron content. Upon increasing the temperature up to 2500 °C, Xirr decreases to about 0.1 in the graphitic carbons, while Xrev reaches a minimum of 0.4–0.5 at 1700 °C and next increases to a value close to 1 at 2500 °C. In the boron doped graphite, Xirr has a slight tendency to increase with the boron content, due to the simultaneous presence of nitrogen in these materials and their strong affinity for oxygen from the atmosphere.

We also recommend Trading Suppliers and Manufacturers of Borane-pyridine complex (cas 110-51-0). Pls Click Website Link as below: cas 110-51-0 suppliers