The capillary extrusion property of ethylene–tetrafluoroethylene copolymer (ETFE) is evaluated. It is found that ETFE shows several types of flow instabilities. The shark-skin failure is observed over the first critical shear stress 7.9 × 104 Pa. Then, the slip-stick instability is detected at 1.8 × 105 Pa, which corresponds to the critical stress of the slippage at the die wall, evaluated by the Mooney method. Moreover, gross wavy melt fracture appears at high out-put rate condition. It is interesting to note that quasi-stable flow region; so-called “super-extrusion”, is observed between slip-stick and wavy melt fracture regions. Because of the steady slippage, ETFE can be extruded at a high out-put rate condition without surface roughness and distortion of extrudates.
We also recommend Trading Suppliers and Manufacturers of Tetrafluoroethylene (cas 116-14-3). Pls Click Website Link as below: cas 116-14-3 suppliers
About|Contact|Cas|Product Name|Molecular|Country|Encyclopedia
Message|New Cas|MSDS|Service|Advertisement|CAS DataBase|Article Data|Manufacturers | Chemical Catalog
©2008 LookChem.com,License: ICP
NO.:Zhejiang16009103
complaints:service@lookchem.com Desktop View