Add time:07/18/2019         Source:sciencedirect.com

Polymer/reduced graphite oxide (rGO) composite nanoparticles with a high electrical conductivity were synthesized using the miniemulsion polymerization technique. The rGO was modified with a reactive surfactant, 2-acrylamido-2-methyl-1-propanesulfonic acid (AMPS), to facilitate monomer intercalation into the rGO nanogalleries. The AMPS-modified rGO was emulsified in the presence of styrene (St) and butyl acrylate (BA) monomers, and the stable miniemulsion was polymerized to form poly(St-co-BA)/rGO composite latex nanoparticles. The transition in the composite nanoparticles from an electrical insulator to an electrical conductor occurred at an rGO content of 10 wt% (relative to the monolayer content), yielding an electrical conductivity of 0.49 S/cm. The electrical conductivity of the composite nanoparticles reached 2.22 S/cm at 20 wt% rGO, yielding a much better conductivity than other polymer composites prepared using a GO filler. Importantly, the miniemulsion polymerization method for fabricating poly(St-co-BA)/rGO composite nanoparticles is easy, green, low-cost, and scalable, providing a universal route to the rational design and engineering of highly conductive polymer composites.

We also recommend Trading Suppliers and Manufacturers of POLY(2-ACRYLAMIDO-2-METHYL-1-PROPANESULFONIC ACID-CO-STYRENE) (cas 51121-85-8). Pls Click Website Link as below: cas 51121-85-8 suppliers