W-containing mesocellular silica foams (MCF) having a Si/W (molar) ratio of 10–40 were synthesized and characterized by means of N2 adsorption, SAXS, XRD, TEM, DRIFTS, DR UV–vis and Raman spectroscopy. The results show that tungsten was well incorporated inside the MCF material and the nature of WOx species closely depends on the tungsten content. At low tungsten content (Si/W ≥ 20), the characteristic mesocellular structure of the MCF material was well maintained while at higher tungsten content (Si/W ∼ 10) a significant degradation of the mesocellular arrangement of MCF pores was observed. The selective liquid-phase oxidation of 1,3-butanediol (1,3-BDO) to 4-hydroxy-2-butanone (HB) over the W-MCF material with various Si/W ratios was investigated. Under optimized reaction conditions, the W-MCF catalyst showed a superior catalytic performance in the selective oxidation of 1,3-BDO as compared to other W-containing materials such as WO3/MCF and W-SBA-15. Moreover, a very stable catalytic activity as a function of cycling test was observed for the W-MCF catalyst.
We also recommend Trading Suppliers and Manufacturers of 2-Butanone peroxide (cas 1338-23-4). Pls Click Website Link as below: cas 1338-23-4 suppliers
About|Contact|Cas|Product Name|Molecular|Country|Encyclopedia
Message|New Cas|MSDS|Service|Advertisement|CAS DataBase|Article Data|Manufacturers | Chemical Catalog
©2008 LookChem.com,License: ICP
NO.:Zhejiang16009103
complaints:service@lookchem.com Desktop View