Using an in-situ polymerization method, poly (methyl methacrylate) (PMMA) cross-linked by Trimethylolpropane triacrylate (cas 15625-89-5) (TMPTA) was embedded with nanosilica, aluminum oxide, or modified montmorillonite to produce various cross-linked nanocomposites. The same three nanofillers were also embedded into PMMA without TMPTA cross-linkages to quantify the effect of TMPTA cross-linkages on the thermal stability and char yield of nanocomposites. Data from Thermogravimetric Analysis (TGA) and Derivative Thermogravimetric Analysis (DTG) were used to show that cross-linking and nanofiller content act synergistically to improve the thermal stability of PMMA, increasing the on-set of degradation by nearly 100 °C. The increase in thermal stability was attributed to the elimination of low temperature end initiated polymer unzipping by TMPTA cross-linkages and simultaneous stabilization of remaining degradation reactions due to nanofiller content. Char formed during a fire accumulates on the surface of the nanocomposite, forming a barrier that protects any unburned material below the surface. The DTG data showed nanocomposites containing 1 wt% silica in PMMA cross-linked by TMPTA produced 14.1% char residues, while nanocomposites without TMPTA cross-linkages required five times the mass of nanofiller to achieve similar yields.

We also recommend Trading Suppliers and Manufacturers of Trimethylolpropane triacrylate (cas 15625-89-5). Pls Click Website Link as below: cas 15625-89-5 suppliers