To widen the applications of conventional reactive melt infiltration (RMI) in large-sized complex-shaped C/C components, an ingenious process of gel-RMI (GRMI) was proposed in this study. The arching C/CSiC composite was prepared successfully using GRMI method with polycarbosilane (PCS)Si90Zr10 (Si: 90 at.%; Zr:10 at.%) sol. The porosity rate of the C/C preform decreased from 18.5% to 2.9%, while the density was raised from 1.40 g·cm−3 to 2.05 g·cm−3 after GRMI. The reason why C/C preform has been significantly densified is as follow: the PCS in PCS-Si90Zr10 sol formed SiC aerogel skeleton after pyrolysis, and then the Si90Zr10 powders were melted and released from the SiC aerogel into the C/C preform body when the temperature reached the melting point of Si90Zr10 alloy. The obtained C/CSiC composite showed a pseudo-ductile rupture characteristic distinguished from that of the C/C preform, and its bending strength was significantly improved from 104.2 MPa of the C/C preform to 258.8 MPa. The C/CSiC composite had a far lower mass ablation rate of 0.75 mg·s−1 than that of C/C preform, 23.30 mg·s−1. Moreover, the GRMI was preliminarily applied in ceramic modifying nozzle-like C/C preform, and the result showed that the nozzle-like C/C preform was successfully densified from 1.3 g cm−3 to 1.96 g cm−3. The GRMI process has great potential in ceramic modifying large-sized complex-shaped C/C components.

We also recommend Trading Suppliers and Manufacturers of (-)-Bakkenolide C (cas 18456-00-3). Pls Click Website Link as below: cas 18456-00-3 suppliers