This paper reports the synthesis of large plate-like gypsum (calcium sulfate) dihydrate generated from waste gypsum board via a wet process. Gypsum hemihydrate was formed by dehydrating waste gypsum board in a sodium sulfate solution at 100 °C for 1 h to form needle-like crystals. The large gypsum dihydrate was formed by lowering the temperature of the gypsum hemihydrate suspension below 80 °C. The large plate-like gypsum dihydrate was obtained by adding seed crystals to a suspension cooled at 80 °C. When 40 μm seed crystals were added at 0.5 mass%, the large plate-like gypsum dihydrate crystals obtained from waste gypsum board had average dimensions of 250 μm length × 100 μm width × 35 μm thickness.
We also recommend Trading Suppliers and Manufacturers of Magnesium nitrate dihydrate. (cas 15750-45-5). Pls Click Website Link as below: cas 15750-45-5 suppliers
About|Contact|Cas|Product Name|Molecular|Country|Encyclopedia
Message|New Cas|MSDS|Service|Advertisement|CAS DataBase|Article Data|Manufacturers | Chemical Catalog
©2008 LookChem.com,License: ICP
NO.:Zhejiang16009103
complaints:service@lookchem.com Desktop View