Add time:09/08/2019         Source:sciencedirect.com

An aluminum material stabilized with a 1.6 vol% of nanometric Al2O3 dispersoids, named HITEMAL, was fabricated by hot extrusion of a fine atomized Al powder. The Al2O3 dispersoids stemmed from a native Al2O3 films on an aluminum powder surface. An extruded rod of the material was then cold-deformed out into a thin wire by rotatory swaging, hydro extrusion and rolling. Such severely deformed HITEMAL was studied as a prospective outer sheath stabilizer material for MgB2 core superconductor wires. An emphasis was put on the effect of annealing realized at various temperatures close to the melting point of Al, which is typically applied to form an in-situ MgB2 superconductive core, on the mechanical and electrical properties of the HITEMAL wire. A systematic investigation was performed of changes to a severely deformed Al grain structure and Al2O3 dispersoids upon annealing the as-deformed wire from 595 to 655 °C for 30 min. Mechanical and electrical properties of the wire were measured at room and cryogenic temperatures. The results showed that the ultrafine-grained Al + 1.6 vol% Al2O3 wire exhibited advantageous properties, and surface integrity after annealing up to 642 °C. It is thus a lightweight material of choice for outer sheaths of MgB2 superconductors.

We also recommend Trading Suppliers and Manufacturers of D 595 (cas 16740-29-7). Pls Click Website Link as below: cas 16740-29-7 suppliers