New CrAlSBA-15 mesoporous materials have been prepared by direct synthesis and characterized by ICP-AES, XRD, N2 adsorption, 27Al NMR, TEM, UV–vis and H2-TPR. CrAlSBA-15 materials exhibited high mesostructural order starting from chromium(III) nitrate (Si/Cr = 66; Si/Al = 35 at pH 3) and from chromium(III) acetate hydroxide (Si/Cr = 39; Si/Al = 51 at pH 1.5). The incorporation of chromium and aluminium into SBA-15 mesoporous structure is enhanced by increasing the pH and produces an increase in pore size and pore volume. After calcination, samples prepared by one-step synthesis showed Cr(VI) centres well dispersed with a proportion of chromate species higher than Cr/AlSBA-15 catalysts prepared by impregnation and grafting. H2-TPR measurements showed that only the 80% of Cr(VI) ions incorporated into the SBA-15 structure were reduced, so part of chromium ions may be located in non-accessible positions inside the solid walls.CrAlSBA-15 materials obtained by direct synthesis exhibited higher ethylene polymerization activity (381.1 kg PE/g Cr h) than Cr/AlSBA-15 and conventional Cr/SiO2 Phillips catalyst prepared by impregnation (260.5 and 216 kg PE/g Cr h, respectively).
We also recommend Trading Suppliers and Manufacturers of chromium dichloride hydroxide (cas 14982-80-0). Pls Click Website Link as below: cas 14982-80-0 suppliers
About|Contact|Cas|Product Name|Molecular|Country|Encyclopedia
Message|New Cas|MSDS|Service|Advertisement|CAS DataBase|Article Data|Manufacturers | Chemical Catalog
©2008 LookChem.com,License: ICP
NO.:Zhejiang16009103
complaints:service@lookchem.com Desktop View