Hybrid monolithic materials were prepared through polymerisation of 2-hydroxyethyl methacrylate (HEMA) mixed with zirconium alkoxides (Zr(OBun)4, Zr(OPrn)4 and Zr(OEt)4), modified by acetylacetonate groups. The molar ratio HEMA/Zr varied between 1 and 4. Thermo-Gravimetry coupled with Mass Spectroscopy (TG-MS) analyses, 13C MAS NMR and Dynamical Mechanical Thermal Analysys (DMTA) indicated the polymeric chains were interconnected by the inorganic component.The presence of zirconium alkoxides modified substantially the poly-HEMA properties. Glass transition temperature of hybrid materials derived from butoxy and propoxy was found in the range 50–80 °C, depending on the composition. The typical swelling of p-HEMA in the water, was suppressed by the presence of zirconium compounds. After immersion in distilled water, hybrid polymers showed an initial slight weight increase, followed by a small mass loss, which increases proportionally to the length of alkoxyl group (ethoxide(propoxide(butoxide) and reaches a constant value after about 40 days. The hybrids remained always rigid and transparent. Flexural modulus and strength of about 400–900 and 4–8 MPa were measured.
We also recommend Trading Suppliers and Manufacturers of Zirconium methacrylate (cas 67893-01-0). Pls Click Website Link as below: cas 67893-01-0 suppliers
About|Contact|Cas|Product Name|Molecular|Country|Encyclopedia
Message|New Cas|MSDS|Service|Advertisement|CAS DataBase|Article Data|Manufacturers | Chemical Catalog
©2008 LookChem.com,License: ICP
NO.:Zhejiang16009103
complaints:service@lookchem.com Desktop View