The trimethylsilylester of β-(4-acetoxyphenyl) propionic acid (APPA), which is easier to isolate than the free acid, was used as monomer for all polycondensations. Copolycondensations with small amounts of 4-tert-butylbenzoic acid or 4-tert-butylphenol acetate yielded oligo- and polyesters with two different endgroups. All oligoesters show a reversible first order phase transition between 240 and 265°C yielding a solid mesophase upon heating. The formation of an isotropic melt occurs between 340 and 380°C depending on the degree of polymerization (DP). The glasstransition temperatures increased from 48–50°C to values around 63–65°C with increasing molecular weight. Copolycondensations with acetylated bisphenol-P yielded telechelic oligoesters with two identical endgroups. Four-armed star-shaped polyesters were prepared by copolycondensation of a tetraacetoxyspirobisindan. Since the bisphenol-P and the spirobisindane units are unfavourable for the crystallization, the crystallinity depends on the DP, and the solubility depends in turn on the crystallinity. Hyperbranched copolyesters were synthesized by copolycondensation of silylated APPA with silylated or free 3,5-bisacetoxybenzoic acid with variation of the molar ratio. The hyperbranched character of these copolyesters was demonstrated by their reluctance to crystallize and by 13C n.m.r. spectroscopic sequence analyses. The Tgs of these hyperbranched copolyesters follow almost exactly the Fox equation. G.p.c. measurements revealed number average molecular weights (Mn) up to 31 000 g mol−1 (for the 11 copolyester) and Mw/Mn ratios in the range of 3.5–6.5.

We also recommend Trading Suppliers and Manufacturers of 3-(2-ACETOXYPHENYL)PROPIONIC ACID (cas 17123-74-9). Pls Click Website Link as below: cas 17123-74-9 suppliers