The changes of the surface morphology of poly(tetrafluoroethylene) due to proton irradiation was investigated. 1 MeV proton beam was used for the irradiations with relatively low current densities, in the range of 10–100,000 pA/mm2. The applied ion fluences ranged from 0.1 to 2500 nC/mm2 (6.24 * 1010–1.56 * 1015 ion/cm2). The surface was characterized by interference contrast microscopy, surface profilometry and scanning electron microscopy. The results show that at each current density the surface can be machined, and the etching depth is increasing with increasing ion fluence, up to a certain point. However, in each case there is a threshold value, between 50 and 100 nC/mm2, where the process turns back. First, the etching depth starts to decrease. Later, by further increasing the delivered ion fluence, an opposite process begins and the surface becomes protruding.
We also recommend Trading Suppliers and Manufacturers of Tetrafluoroethylene (cas 116-14-3). Pls Click Website Link as below: cas 116-14-3 suppliers
About|Contact|Cas|Product Name|Molecular|Country|Encyclopedia
Message|New Cas|MSDS|Service|Advertisement|CAS DataBase|Article Data|Manufacturers | Chemical Catalog
©2008 LookChem.com,License: ICP
NO.:Zhejiang16009103
complaints:service@lookchem.com Desktop View