The mechanical properties of zirconium hydrides were studied using nano-indentation technique between 25 and 400 °C. Temperature dependency of reduced elastic modulus and hardness of δ- and ε-zirconium hydrides were obtained by conducting nanoindentation experiments on bulk hydride samples with independently heating capability of indenter and heating stage. The reduced elastic modulus of δ-zirconium hydride (H/Zr ratio = 1.61) decreased from ∼113 GPa at room temperature to ∼109 GPa at 400 °C, while its hardness decreased significantly from 4.1 GPa to 2.41 GPa in the same temperature range. For ε-zirconium hydrides (H/Zr ratio = 1.79), the reduced elastic modulus decreased from 61 GPa at room temperature to 54 GPa at 300 °C, while its hardness from 3.06 GPa to 2.19 GPa.
We also recommend Trading Suppliers and Manufacturers of Zirconium hydride (cas 11105-16-1). Pls Click Website Link as below: cas 11105-16-1 suppliers
About|Contact|Cas|Product Name|Molecular|Country|Encyclopedia
Message|New Cas|MSDS|Service|Advertisement|CAS DataBase|Article Data|Manufacturers | Chemical Catalog
©2008 LookChem.com,License: ICP
NO.:Zhejiang16009103
complaints:service@lookchem.com Desktop View