(3-chloropropyl)triethoxysilane
bis(3-triethoxysilylpropyl) tetrasulfide
Conditions | Yield |
---|---|
With sodium polysulfide In ethanol at 78℃; Product distribution / selectivity; | 97.8% |
With sodium sulfide; sodium hydrogencarbonate; sulfur In ethanol; water | |
With sodium sulfide; sulfur In ethanol; toluene for 4h; Reflux; Green chemistry; | |
With sodium sulfide; sodium borate; dodecyltrimethylammonium bromide; sulfur; potassium iodide In water at 40 - 55℃; for 1h; Temperature; Reagent/catalyst; |
(3-chloropropyl)triethoxysilane
A
bis(3-triethoxysilylpropyl) tetrasulfide
B
4,4,13,13-tetraethoxy-3,14-dioxa-8,9-dithia-4,13-disilahexadecane
C
4,4,14,14-tetraethoxy-3,15-dioxa-8,9,10-trithia-4,14-disilaheptadecane
Conditions | Yield |
---|---|
With sodium oligosulfide In 1,2-dimethoxyethane for 1h; Heating; Further byproducts given; |
(3-chloropropyl)triethoxysilane
D
bis(3-triethoxysilylpropyl) tetrasulfide
E
bis-[γ-(triethoxysilyl)propyl]sulfide
F
4,4,13,13-tetraethoxy-3,14-dioxa-8,9-dithia-4,13-disilahexadecane
G
4,4,14,14-tetraethoxy-3,15-dioxa-8,9,10-trithia-4,14-disilaheptadecane
Conditions | Yield |
---|---|
Stage #1: (3-chloropropyl)triethoxysilane With sulfur at 80℃; Stage #2: With sodium trisulfide; tetrabutylammomium bromide In water at 80 - 90℃; for 3.66667h; Product distribution / selectivity; | |
Stage #1: (3-chloropropyl)triethoxysilane With sulfur at 80℃; Stage #2: With sodium sulfide; tetrabutylammomium bromide In water at 80 - 90℃; for 3.66667h; Product distribution / selectivity; |
(3-chloropropyl)triethoxysilane
C
bis(3-triethoxysilylpropyl) tetrasulfide
D
bis-[γ-(triethoxysilyl)propyl]sulfide
E
4,4,13,13-tetraethoxy-3,14-dioxa-8,9-dithia-4,13-disilahexadecane
F
4,4,14,14-tetraethoxy-3,15-dioxa-8,9,10-trithia-4,14-disilaheptadecane
Conditions | Yield |
---|---|
Stage #1: (3-chloropropyl)triethoxysilane With sulfur In toluene at 80℃; Stage #2: With tetrabutylammomium bromide; sulfur In water; toluene at 80 - 85℃; for 5.58333h; Product distribution / selectivity; | |
With sodium sulfide; tetrabutylammomium bromide; sulfur In water at 80 - 90℃; for 6.66667h; Product distribution / selectivity; | |
Stage #1: (3-chloropropyl)triethoxysilane With sodium sulfide; tetrabutylammomium bromide; sulfur In water at 80 - 90℃; for 8.66667h; Stage #2: With tetrabutylammomium bromide; sulfur In water; toluene at 80 - 85℃; for 5.58333h; Product distribution / selectivity; | |
Stage #1: (3-chloropropyl)triethoxysilane With sulfur In toluene at 80℃; Stage #2: With sodium sulfide; tetrabutylammomium bromide In water; toluene at 90 - 95℃; for 5.75h; Product distribution / selectivity; |
(3-chloropropyl)triethoxysilane
B
bis(3-triethoxysilylpropyl) tetrasulfide
C
bis-[γ-(triethoxysilyl)propyl]sulfide
D
4,4,13,13-tetraethoxy-3,14-dioxa-8,9-dithia-4,13-disilahexadecane
E
4,4,14,14-tetraethoxy-3,15-dioxa-8,9,10-trithia-4,14-disilaheptadecane
Conditions | Yield |
---|---|
With sodium sulfide; tetrabutylammomium bromide; sulfur In water at 80 - 90℃; for 5.66667h; Product distribution / selectivity; | |
Stage #1: (3-chloropropyl)triethoxysilane With tetrabutylammomium bromide; sulfur at 80℃; Stage #2: With sodium sulfide; tetrabutylammomium bromide In water at 70 - 80℃; for 5.83333h; Product distribution / selectivity; | |
Stage #1: (3-chloropropyl)triethoxysilane With sulfur at 80℃; Stage #2: With sodium sulfide; tetrabutylammomium bromide In water at 80 - 90℃; for 5.58333h; Product distribution / selectivity; | |
Stage #1: (3-chloropropyl)triethoxysilane With tetrabutylammomium bromide In water at 80℃; Stage #2: With sodium sulfide; sulfur In water at 70 - 80℃; for 5.66667h; Product distribution / selectivity; |
bis(3-triethoxysilylpropyl) tetrasulfide
Conditions | Yield |
---|---|
With disodium tetrasulfide In ethanol | |
With sodium sulfide; hydrogen sulfide In ethanol |
(n-pr-1-Cl)SiCl3
bis(3-triethoxysilylpropyl) tetrasulfide
Conditions | Yield |
---|---|
With disodium tetrasulfide In ethanol | |
With sodium sulfide; hydrogen sulfide In ethanol | |
With disodium tetrasulfide In ethanol | |
With disodium tetrasulfide In ethanol |
(3-chloropropyl)triethoxysilane
bis(3-triethoxysilylpropyl) tetrasulfide
Conditions | Yield |
---|---|
With sodium sulfide nonahydrate; hydrogen sulfide; nitrogen In water; toluene |
(3-chloropropyl)triethoxysilane
A
bis(3-triethoxysilylpropyl) tetrasulfide
B
4,4,13,13-tetraethoxy-3,14-dioxa-8,9-dithia-4,13-disilahexadecane
C
4,4,14,14-tetraethoxy-3,15-dioxa-8,9,10-trithia-4,14-disilaheptadecane
Conditions | Yield |
---|---|
With sodium hydrogen sulfide monohydrate; sodium carbonate; sulfur; sodium hydroxide In ethanol; water at 65 - 75℃; Product distribution / selectivity; | |
With sodium hydrogen sulfide monohydrate; sodium carbonate; sulfur; sodium hydroxide In ethanol; water at 65 - 75℃; Product distribution / selectivity; |
bis(3-triethoxysilylpropyl) tetrasulfide
diethylene glycol
bis[tri(hydroxydiethyleneoxy)silylpropyl] tetrasulfide
Conditions | Yield |
---|---|
With sodium ethanolate In ethanol at 150℃; under 20 Torr; for 2h; | 99% |
triethanolamine
bis(3-triethoxysilylpropyl) tetrasulfide
1,1'-(tetrathiodi-3,1-propanediyl)bis-2,8,9-trioxa-5-aza-1-silabicyclo[3.3.3]undecane
Conditions | Yield |
---|---|
sodium ethanolate In ethanol at 150℃; under 200 Torr; for 2h; | 98% |
2-methyl-2,4-pentanediol
bis(3-triethoxysilylpropyl) tetrasulfide
Conditions | Yield |
---|---|
sulfuric acid at 41 - 49℃; under 50 - 80 Torr; for 4h; | 86.5% |
1,1,1,3,5,5,5-heptamethyltrisiloxan
bis(3-triethoxysilylpropyl) tetrasulfide
Conditions | Yield |
---|---|
With tris(pentafluorophenyl)borate In toluene for 3h; Inert atmosphere; | 59% |
Conditions | Yield |
---|---|
toluene-4-sulfonic acid at 95 - 100℃; for 4h; Conversion of starting material; | |
tetrabutoxytitanium at 110 - 130℃; for 3h; Conversion of starting material; |
Conditions | Yield |
---|---|
toluene-4-sulfonic acid at 110 - 120℃; for 4h; Conversion of starting material; |
Conditions | Yield |
---|---|
tetrabutoxytitanium at 120℃; under 15.0015 - 600.06 Torr; for 4.5h; Conversion of starting material; |
bis(3-triethoxysilylpropyl) tetrasulfide
n-octanoic acid chloride
A
3-(octanoylsulfanyl)-1-propyltriethoxysilane
B
octanoic acid ethyl ester
C
(3-chloropropyl)triethoxysilane
D
3-Mercaptopropyltriethoxysilane
E
bis-[γ-(triethoxysilyl)propyl]sulfide
F
4,4,13,13-tetraethoxy-3,14-dioxa-8,9-dithia-4,13-disilahexadecane
G
4,4,14,14-tetraethoxy-3,15-dioxa-8,9,10-trithia-4,14-disilaheptadecane
Conditions | Yield |
---|---|
Stage #1: bis(3-triethoxysilylpropyl) tetrasulfide With sodium In Solvent 140 at 110℃; for 0.75h; Stage #2: n-octanoic acid chloride In Solvent 140 at 45 - 104℃; for 1h; Stage #3: With water In toluene at 45℃; Product distribution / selectivity; |
bis(3-triethoxysilylpropyl) tetrasulfide
bis[3-(trihydroxysilyl)propyl]-tetrasulfide
Conditions | Yield |
---|---|
With acetic acid In ethanol; water for 24h; pH=4.5; |
bis(3-triethoxysilylpropyl) tetrasulfide
allyltriethoxysilane
Conditions | Yield |
---|---|
at 590℃; for 0.00138889h; Pyrolysis; |
The Bis[3-(triethoxysilyl)propyl]tetrasulfide is an organic compound with the formula C18H42O6S4Si2. The IUPAC name of this chemical is triethoxy-[3-(3-triethoxysilylpropyltetrasulfanyl)propyl]silane. With the CAS registry number 40372-72-3, it is also named as 4,4,15,15-Tetraethoxy-3,16-dioxa-8,9,10,11-tetrathia-4,15-disilaoctadecane. The product's categories are Industrial/Fine Chemicals; Sulfur; Adhesion Promoters; Coupling Agents; Dispersing Agents; Sulfur Silanes; Surface Modifiers. Besides, it is a yellowish clear liquid, which should be stored in a closed cool and dry place. It is widely used in radial tires and rubber tire tread, carcass, tire wall, solid rubber tires and other rubber products.
Physical properties about Bis[3-(triethoxysilyl)propyl]tetrasulfide are: (1)ACD/LogP: 8.04; (2)# of Rule of 5 Violations: 2; (3)ACD/LogD (pH 5.5): 8.04; (4)ACD/LogD (pH 7.4): 8.04; (5)ACD/BCF (pH 5.5): 757450.06; (6)ACD/BCF (pH 7.4): 757450.06; (7)ACD/KOC (pH 5.5): 562356.13; (8)ACD/KOC (pH 7.4): 562356.13; (9)#H bond acceptors: 6; (10)#Freely Rotating Bonds: 23; (11)Polar Surface Area: 156.58 Å2; (12)Index of Refraction: 1.503; (13)Molar Refractivity: 145.33 cm3; (14)Molar Volume: 491.1 cm3; (15)Polarizability: 57.61×10-24cm3; (16)Surface Tension: 34.1 dyne/cm; (17)Density: 1.097 g/cm3; (18)Flash Point: 262 °C; (19)Enthalpy of Vaporization: 75.07 kJ/mol; (20)Boiling Point: 509.6 °C at 760 mmHg; (21)Vapour Pressure: 5.34E-10 mmHg at 25°C.
When you are using this chemical, please be cautious about it as the following:
When you are using it, avoid contact with skin and eyes and do not breathe gas/fumes/vapour/spray (appropriate wording to be specified by the manufacturer).
You can still convert the following datas into molecular structure:
(1)SMILES: O(CC)[Si](OCC)(OCC)CCCSSSSCCC[Si](OCC)(OCC)OCC
(2)InChI: InChI=1/C18H42O6S4Si2/c1-7-19-29(20-8-2,21-9-3)17-13-15-25-27-28-26-16-14-18-30(22-10-4,23-11-5)24-12-6/h7-18H2,1-6H3
(3)InChIKey: VTHOKNTVYKTUPI-UHFFFAOYAN
(4)Std. InChI: InChI=1S/C18H42O6S4Si2/c1-7-19-29(20-8-2,21-9-3)17-13-15-25-27-28-26-16-14-18-30(22-10-4,23-11-5)24-12-6/h7-18H2,1-6H3
(5)Std. InChIKey: VTHOKNTVYKTUPI-UHFFFAOYSA-N
About|Contact|Cas|Product Name|Molecular|Country|Encyclopedia
Message|New Cas|MSDS|Service|Advertisement|CAS DataBase|Article Data|Manufacturers | Chemical Catalog
©2008 LookChem.com,License: ICP
NO.:Zhejiang16009103
complaints:service@lookchem.com Desktop View