Conditions | Yield |
---|---|
With pyridine In diethyl ether at 35℃; for 4h; | 77% |
Conditions | Yield |
---|---|
With sulfur trioxide; copper at 80 - 130℃; Zufuegen von Wasser, Kochen und folgendes Erhitzen des Reaktionsgemisches mit Aethylenglykol-monoaethylaether auf 100-110grad; |
2-ethoxy-ethanol
methacrylic acid methyl ester
2-ethoxyethyl methacrylate
Conditions | Yield |
---|---|
With sulfuric acid | |
With sodium 2-ethoxyethoxide | |
With sodium 2-ethoxyethoxide |
2-ethoxy-ethanol
1,2-propanediene
carbon monoxide
2-ethoxyethyl methacrylate
Conditions | Yield |
---|---|
dodecacarbonyl-triangulo-triruthenium at 100℃; under 11400 Torr; for 3h; | 80 % Chromat. |
methyl 2-methoxy-2-methylpropanoate
2-ethoxyethyl methacrylate
Conditions | Yield |
---|---|
Multi-step reaction with 2 steps 1: anhydrous oxalic acid; hydroquinone 2: H2SO4 View Scheme |
2-ethoxyethyl methacrylate
2-(naphthalen-1-yl)benzenamine
Conditions | Yield |
---|---|
With disodium hydrogenphosphate; (S)-STRIP; palladium diacetate; silver sulfate In toluene at 60℃; for 48h; Schlenk technique; stereoselective reaction; | 61% |
Conditions | Yield |
---|---|
With bis(acetylacetonate)nickel(II) In toluene |
Conditions | Yield |
---|---|
With bis(acetylacetonate)nickel(II) In toluene |
Conditions | Yield |
---|---|
With potassium peroxomonosulphate; sodium dodecyl-sulfate In cyclohexane; water at 60 - 70℃; for 3.5h; Product distribution; different ratios of monomers and solvent; |
2-ethoxyethyl methacrylate
polymer, radical copolymerization; monomer(s): 4-[4-(2-methyl-acryloyloxy)-phenyl]-2,6-diphenyl-pyranylium tetrafluoroborate; 2-ethoxyethyl methacrylate, molar ratio 0.5:100
Conditions | Yield |
---|---|
With 2,2'-azobis(isobutyronitrile); EDMA at 65℃; for 5h; |
2-ethoxyethyl methacrylate
polymer, radical copolymerization; monomer(s): 4-[4-(2-methyl-acryloyloxy)-phenyl]-2,6-diphenyl-pyranylium tetrafluoroborate; 2-ethoxyethyl methacrylate, molar ratio 1.0:100
Conditions | Yield |
---|---|
With 2,2'-azobis(isobutyronitrile); EDMA at 65℃; for 5h; |
2-ethoxyethyl methacrylate
polymer, radical copolymerization; monomer(s): 4-[4-(2-methyl-acryloyloxy)-phenyl]-2,6-diphenyl-pyranylium tetrafluoroborate; 2-ethoxyethyl methacrylate, molar ratio 2.0:100
Conditions | Yield |
---|---|
With 2,2'-azobis(isobutyronitrile); EDMA at 65℃; for 5h; |
2-ethoxyethyl methacrylate
2,3-dihydroxypropyl methacrylate
polymer, radical copolymerization; monomer(s): 4-[4-(2-methyl-acryloyloxy)-phenyl]-2,6-diphenyl-pyranylium tetrafluoroborate; 2-ethoxyethyl methacrylate; 2,3-dihydroxypropyl methacrylate, molar ratio 0.5:75:25
Conditions | Yield |
---|---|
With 2,2'-azobis(isobutyronitrile); EDMA at 65℃; for 5h; |
2-ethoxyethyl methacrylate
2,3-dihydroxypropyl methacrylate
polymer, radical copolymerization; monomer(s): 4-[4-(2-methyl-acryloyloxy)-phenyl]-2,6-diphenyl-pyranylium tetrafluoroborate; 2-ethoxyethyl methacrylate; 2,3-dihydroxypropyl methacrylate, molar ratio 1.0:75:25
Conditions | Yield |
---|---|
With 2,2'-azobis(isobutyronitrile); EDMA at 65℃; for 5h; |
2-ethoxyethyl methacrylate
2,3-dihydroxypropyl methacrylate
polymer, radical copolymerization; monomer(s): 4-[4-(2-methyl-acryloyloxy)-phenyl]-2,6-diphenyl-pyranylium tetrafluoroborate; 2-ethoxyethyl methacrylate; 2,3-dihydroxypropyl methacrylate, molar ratio 2.0:75:25
Conditions | Yield |
---|---|
With 2,2'-azobis(isobutyronitrile); EDMA at 65℃; for 5h; |
2-ethoxyethyl methacrylate
2,3-dihydroxypropyl methacrylate
polymer, radical copolymerization; monomer(s): 4-[4-(2-methyl-acryloyloxy)-phenyl]-2,6-diphenyl-pyranylium tetrafluoroborate; 2-ethoxyethyl methacrylate; 2,3-dihydroxypropyl methacrylate, molar ratio 0.5:50:50
Conditions | Yield |
---|---|
With 2,2'-azobis(isobutyronitrile); EDMA at 65℃; for 5h; |
2-ethoxyethyl methacrylate
2,3-dihydroxypropyl methacrylate
polymer, radical copolymerization; monomer(s): 4-[4-(2-methyl-acryloyloxy)-phenyl]-2,6-diphenyl-pyranylium tetrafluoroborate; 2-ethoxyethyl methacrylate; 2,3-dihydroxypropyl methacrylate, molar ratio 1.0:50;50
Conditions | Yield |
---|---|
With 2,2'-azobis(isobutyronitrile); EDMA at 65℃; for 5h; |
2-ethoxyethyl methacrylate
2,3-dihydroxypropyl methacrylate
polymer, radical copolymerization; monomer(s): 4-[4-(2-methyl-acryloyloxy)-phenyl]-2,6-diphenyl-pyranylium tetrafluoroborate; 2-ethoxyethyl methacrylate; 2,3-dihydroxypropyl methacrylate, molar ratio 2.0:50:50
Conditions | Yield |
---|---|
With 2,2'-azobis(isobutyronitrile); EDMA at 65℃; for 5h; |
Conditions | Yield |
---|---|
With 2,2'-azobis(isobutyronitrile) at 70℃; for 5h; |
Conditions | Yield |
---|---|
With 2,2'-azobis(isobutyronitrile) at 70℃; for 5h; |
Conditions | Yield |
---|---|
With 2,2'-azobis(isobutyronitrile) at 70℃; for 5h; |
Conditions | Yield |
---|---|
With 2,2'-azobis(isobutyronitrile) at 70℃; for 5h; |
Conditions | Yield |
---|---|
With 2,2'-azobis(isobutyronitrile) at 70℃; for 5h; |
Conditions | Yield |
---|---|
With 2,2'-azobis(isobutyronitrile) at 70℃; for 5h; |
2-ethoxyethyl methacrylate
Conditions | Yield |
---|---|
With 2,2-dimethoxy-2-phenylacetophenone at 25℃; UV-irradiation; |
2-ethoxyethyl methacrylate
EDMA
2,3-dihydroxypropyl methacrylate
polymer, product of radical copolymerization; monomer(s): 2,6-diphenyl-4-[4-(2-methylacryloyloxy)-phenyl]-pyrylium tetrafluoroborate; 2-ethoxyethyl methacrylate; 2,3-dihydroxypropyl methacrylate; ethyleneglycol dimethacrylate
Conditions | Yield |
---|---|
With 2,2'-azobis(isobutyronitrile) |
2-ethoxyethyl methacrylate
EDMA
2,3-dihydroxypropyl methacrylate
polymer, product of radical copolymerization; monomer(s): 2,6-bis(4-methylphenyl)-4-[4-(2-methylacryloyloxy)-phenyl]-pyrylium tetrafluoroborate; 2-ethoxyethyl methacrylate; 2,3-dihydroxypropyl methacrylate; ethyleneglycol dimethacrylate
Conditions | Yield |
---|---|
With 2,2'-azobis(isobutyronitrile) |
2-ethoxyethyl methacrylate
EDMA
2,3-dihydroxypropyl methacrylate
polymer; monomer(s): 2,6-bis(4-metoxyphenyl)-4-[4-(2-methylacryloyloxy)-phenyl]-pyrylium tetrafluoroborate; 2-ethoxyethyl methacrylate; 2,3-dihydroxypropyl methacrylate; ethyleneglycol dimethacrylate
Conditions | Yield |
---|---|
With 2,2'-azobis(isobutyronitrile) |
The 2-Ethoxyethyl methacrylate with cas registry number of 2370-63-0, belongs to the following product categories: (1)Acrylic Monomers; (2)C8 to C9Monomers; (3)Carbonyl Compounds; (4)Esters; (5)Methacrylate. Its systematic name and IUPAC name are the same, which is 2-ethoxyethyl 2-methylprop-2-enoate.
Physical properties about this chemical are: (1)ACD/LogP: 1.57; (2)# of Rule of 5 Violations: 0; (3)ACD/LogD (pH 5.5): 1.57; (4)ACD/LogD (pH 7.4): 1.57; (5)ACD/BCF (pH 5.5): 9.25; (6)ACD/BCF (pH 7.4): 9.25; (7)ACD/KOC (pH 5.5): 171.01; (8)ACD/KOC (pH 7.4): 171.01; (9)#H bond acceptors: 3; (10)#H bond donors: 0; (11)#Freely Rotating Bonds: 6; (12)Polar Surface Area: 35.53 Å2; (13)Index of Refraction: 1.424; (14)Molar Refractivity: 42.19 cm3; (15)Molar Volume: 165.3 cm3; (16)Polarizability: 16.72×10-24cm3; (17)Surface Tension: 27.9 dyne/cm; (18)Enthalpy of Vaporization: 41.87 kJ/mol; (19)Vapour Pressure: 0.812 mmHg at 25°C.
When you are using this chemical, please be cautious about it as the following:
The 2-Ethoxyethyl methacrylate irritates to eyes, respiratory system and skin. When use it, wear suitable protective clothing, gloves and eye/face protection. If contact with eyes, rinse immediately with plenty of water and seek medical advice. After use it, take off immediately all contaminated clothing.
You can still convert the following datas into molecular structure:
(1)SMILES: O=C(OCCOCC)\C(=C)C;
(2)InChI: InChI=1/C8H14O3/c1-4-10-5-6-11-8(9)7(2)3/h2,4-6H2,1,3H3;
(3)InChIKey: SFPNZPQIIAJXGL-UHFFFAOYAD;
(4)Std. InChI: InChI=1S/C8H14O3/c1-4-10-5-6-11-8(9)7(2)3/h2,4-6H2,1,3H3;
(5)Std. InChIKey: SFPNZPQIIAJXGL-UHFFFAOYSA-N
About|Contact|Cas|Product Name|Molecular|Country|Encyclopedia
Message|New Cas|MSDS|Service|Advertisement|CAS DataBase|Article Data|Manufacturers | Chemical Catalog
©2008 LookChem.com,License: ICP
NO.:Zhejiang16009103
complaints:service@lookchem.com Desktop View