Conditions | Yield |
---|---|
In water pH 7-7.5; 2 h boiling on water bath; filtering, drying; | 94% |
In water pH 7-7.5; 2 h boiling on water bath; filtering, drying; | 94% |
In neat (no solvent, solid phase) for 5 mo; not isolated, detected by XRD; | |
Heating; |
Conditions | Yield |
---|---|
In water H2MoO4*H2O (1 mmol) added to aq. soln. of LiOH*H2O (2 mmol), stirred for20 min; filtered, allowed to stant (air) at room temp. for 1 week; | 87% |
Conditions | Yield |
---|---|
MoO3:Li2CO3 (1:1); reaction begins at 300°C; | |
heating (823 K); |
Conditions | Yield |
---|---|
byproducts: Li; above 1150 °C, Li2O a Mo crucible; | |
at 1320°C, in Mo vessel; | |
at 1320°C, in Mo vessel; |
Conditions | Yield |
---|---|
In neat (no solvent) mixing, firing in air (740K) in a silica crucible fo 48 h with one intermediate grinding; | |
In neat (no solvent) mixing of powdered and dried stoichiometric amounts of starting materials, firing in air at around 740 K for 48 h; |
Conditions | Yield |
---|---|
at 350°C, Li2O:MoO3 mol ratio beetween 1:1 and 2:1; | |
at 350°C, Li2O:MoO3 mol ratio beetween 1:1 and 2:1; |
Conditions | Yield |
---|---|
In water standing (some d); recrystn. (H2O); | |
In neat (no solvent) byproducts: H2O; ground under ambient conditions in air for 1 min, allowed to dry at roomtemp. for ca 1 h; |
Conditions | Yield |
---|---|
With ammonium molybdate In water | |
With ammonium molybdate In water |
Conditions | Yield |
---|---|
above 1150°C; | |
above 1150°C; |
Conditions | Yield |
---|---|
In not given byproducts: CaSO4; equilibrium react. at 25°C;; | |
In not given byproducts: CaSO4; equilibrium react. at 25°C;; |
Conditions | Yield |
---|---|
In neat (no solvent) reaction at 705°C;; | |
In neat (no solvent) reaction at 705°C;; |
Conditions | Yield |
---|---|
In neat (no solvent) accelerated reaction above 705°C;; |
A
lithium molybdate
Conditions | Yield |
---|---|
In neat (no solvent) byproducts: H2O; 149°C; no isolation, monitoring by DTA; |
Conditions | Yield |
---|---|
In neat (no solvent) decomposition at 735°C;; |
Conditions | Yield |
---|---|
In neat (no solvent, solid phase) MoO3, Bi2O3 and Li2CO3, milled for 4.5 h, dried, calcined at 500-550°C for 4 h, remilled for 5 h with H2O, pressed into pellets at 200 MPa with polyvinyl alcohol, sintered at 660°C for 2 h in ambient atm.; monitored by XRD; |
Conditions | Yield |
---|---|
In neat (no solvent, solid phase) stoich. mixt. was initially calcined at 350°C, then annealed for 80-100 h; XRD; |
lithium carbonate
A
lithium molybdate
Conditions | Yield |
---|---|
In melt |
Conditions | Yield |
---|---|
In ethanol at 20℃; |
Conditions | Yield |
---|---|
at 500℃; for 5h; |
Conditions | Yield |
---|---|
at 400℃; for 4h; Temperature; |
Conditions | Yield |
---|---|
In neat (no solvent, solid phase) Li2MoO4, ZnO, MoO2 and Mo powder in stoich. ratio were sealed in an evacuated tube and held at 1100°C for 5 days; ppt. was washed with HCl and deionized water, solid was then dried under vac. at 110°C; elem.anal.; | 90% |
lithium molybdate
iminodiacetic acid
Conditions | Yield |
---|---|
In water aq. soln. of Li2MoO4 (1 mmol) added to aq. soln. of iminodiacetic acid (1 mmol), refluxed for 6 h; filtered, allowed to stand (air) at room temp. for 4 weeks; elem. anal.; | 82% |
lithium molybdate
Methylenediphosphonic acid
water
lithium hydroxide
Conditions | Yield |
---|---|
With N2H4*H2O In water Mo compd. dissolved in HCl soln., N2H4*H2O added, stirred at 60°C, allowed to cool to room temp., Mo compd. and CH2(PO3H2)2 added, LiOH soln. added dropwise until pH 6.0; crystd. at room temp. for 5 d; elem. anal.; | 53% |
lithium molybdate
Methylenediphosphonic acid
water
lithium hydroxide
Conditions | Yield |
---|---|
With N2H4*H2O In water Mo compd. dissolved in HCl soln., N2H4*H2O added, stirred at 60°C, allowed to cool to room temp., LiOH soln. added dropwise until pH 1.5,CH2(PO3H2)2 added, LiOH soln. added dropwise until pH 3.5; crystd. for 5 d; elem. anal.; | 50% |
lithium molybdate
Conditions | Yield |
---|---|
With SnCl2*2H2O In hydrogenchloride addn. of aq. HCl to Li2MoO4 in H2O, addn. of SnCl2*2H2O; storage (20°C, 6 weeks), mechanical sepn. of crystals, washing (filtrated mother-liquor), drying in air on filter paper; | 4% |
Conditions | Yield |
---|---|
In neat (no solvent) Electrolysis; in MoO3 melt contg. 7.5-20 mol % Na2MoO4 + 15.5-3 mol % Li2MoO4, Pt-electrodes, 0.02 to < 1 A cm**-2, 30-100°C over m. p. of electrolyte,6-8 h; washing of product deposited on cathode (hot water); |
lithium molybdate
Conditions | Yield |
---|---|
In neat (no solvent) Electrolysis; in MoO3 melt contg. 3 mol % Na2MoO4 + 20 mol % Li2MoO4, Pt-electrodes, 1A cm**-2, 10-15°C over m. p. of electrolyte, 6-8 h; washing of product mixt. deposited on cathode (hot water); powder X-ray diffraction; |
lithium molybdate
Conditions | Yield |
---|---|
In neat (no solvent) Electrolysis; in MoO3 melt contg. 15.5 mol % Na2MoO4 + 7.5 mol % Li2MoO4, Pt-electrodes, 1 A cm**-2, 10-15°C over m. p. of electrolyte, 6-8 h; washing of product mixt. deposited on cathode (hot water); powder X-ray diffraction; |
lithium molybdate
Conditions | Yield |
---|---|
In neat (no solvent) Electrolysis; in MoO3 melt contg. 13 mol % Na2MoO4 + 10 mol % Li2MoO4, Pt-electrodes, 1 A cm**-2, 10-15°C over m. p. of electrolyte, 6-8 h; washing of product mixt. deposited on cathode (hot water); powder X-ray diffraction; |
Conditions | Yield |
---|---|
In neat (no solvent) Electrolysis; in MoO3 melt contg. 3 mol % Na2MoO4 + 20 mol % Li2MoO4, Pt-electrodes, 0.02 to < 1 A cm**-2, 10-15°C over m. p. of electrolyte, 6-8 h; washing of product deposited on cathode (hot water); |
Conditions | Yield |
---|---|
In neat (no solvent) Electrolysis; in MoO3 melt contg. 15.5 mol % Na2MoO4 + 7.5 mol % Li2MoO4, Pt-electrodes, 0.02 to < 1 A cm**-2, 10-15°C over m. p. of electrolyte, 6-8 h; washing of product deposited on cathode (hot water); |
Conditions | Yield |
---|---|
In neat (no solvent) Electrolysis; in MoO3 melt contg. 13 mol % Na2MoO4 + 10 mol % Li2MoO4, Pt-electrodes,0.02 to < 1 A cm**-2, 10-15°C over m. p. of electrolyte, 6-8 h; washing of product deposited on cathode (hot water); |
Conditions | Yield |
---|---|
In melt Electrolysis; outgassed sample electrolysis (molar ratio MoO3:Li2MoO4=50.5:49.5, crucible, nitrogen flow, 560°C, 6.8 mA, start voltage 1.7 V, 6 d, end voltage 0.6 V); crystals sepn. (crucible soaking into hot dilute HCl); single crystal and powder X-ray diffraction, atomic absorption spectroscopy; | |
In neat (no solvent) Electrolysis; in MoO3 melt contg. 23 mol % Li2MoO4, Pt-electrodes, 0.02 to < 1 A cm**-2, 30-100°C over m. p. of electrolyte, 6-8 h; washing of product deposited on cathode (hot water); |
lithium molybdate
Conditions | Yield |
---|---|
In neat (no solvent) Electrolysis; in MoO3 melt contg. 23 mol % Li2MoO4, Pt-electrodes, 1 A cm**-2, 10-15°C over m. p. of electrolyte, 6-8 h; washing of product mixt. deposited on cathode (hot water); powder X-ray diffraction; |
Conditions | Yield |
---|---|
In melt Electrochem. Process; electrolytic redn. of a melt of Li2MoO4; | |
Electrolysis; electrolysis (0.03 A/cm**2, 4-5 h, 20-25 mol% Li2MoO4); detd. by gravimetry, X-ray photoelectron spectroscopy, laser emission spectroscopy, flame photometry, potentiometric titration; elem. anal.; | |
In neat (no solvent) Electrolysis; in MoO3 melt contg. 23 mol % Li2MoO4, Pt-electrodes, 0.02 to < 1 A cm**-2, 10-15°C over m. p. of electrolyte, 6-8 h; washing of product deposited on cathode (hot water); |
Conditions | Yield |
---|---|
In neat (no solvent) Electrolysis; in MoO3 melt contg. 18-13 mol % K2MoO4 + 5-10 mol % Li2MoO4, Pt-electrodes, 0.02 to < 1 A cm**-2, 30-100°C over m. p. of electrolyte, 6-8h; washing of product deposited on cathode (hot water); |
lithium molybdate
Conditions | Yield |
---|---|
In neat (no solvent) Electrolysis; in MoO3 melt contg. 18 mol % K2MoO4 + 5 mol % Li2MoO4, Pt-electrodes, 1 A cm**-2, 10-15°C over m. p. of electrolyte, 6-8 h; washing of product mixt. deposited on cathode (hot water); powder X-ray diffraction; |
lithium molybdate
Conditions | Yield |
---|---|
In neat (no solvent) Electrolysis; in MoO3 melt contg. 13 mol % K2MoO4 + 10 mol % Li2MoO4, Pt-electrodes, 1A cm**-2, 10-15°C over m. p. of electrolyte, 6-8 h; washing of product mixt. deposited on cathode (hot water); powder X-ray diffraction; |
Conditions | Yield |
---|---|
In neat (no solvent) Electrolysis; in MoO3 melt contg. 18 mol % K2MoO4 + 5 mol % Li2MoO4, Pt-electrodes, 0.02 to < 1 A cm**-2, 10-15°C over m. p. of electrolyte, 6-8 h; washing of product deposited on cathode (hot water); |
Conditions | Yield |
---|---|
In neat (no solvent) Electrolysis; in MoO3 melt contg. 13 mol % K2MoO4 + 10 mol % Li2MoO4, Pt-electrodes, 0.02 to < 1 A cm**-2, 10-15°C over m. p. of electrolyte, 6-8 h; washing of product deposited on cathode (hot water); |
lithium molybdate
molybdenum
Conditions | Yield |
---|---|
In melt Electrolysis; electrolysis of 77.5mol%KF-7.5mol%Li2B4O7-15.0%Li2MoO4 bath, anode: Mo or graphite, cathode: Ni, Cu, Mo, steel or graphite, varying bath temp. and current density; detn. by X-ray; |
Conditions | Yield |
---|---|
In water aq. soln. of 1 mol Li2MoO4 and 5 mol NH4Cl;; crystn.;; |
lithium molybdate
bismuth(III) oxide
Conditions | Yield |
---|---|
In neat (no solvent) melting; |
Conditions | Yield |
---|---|
In melt crystallization from melt;; separation from excess Li2MoO4 with boiling H2O;; |
Conditions | Yield |
---|---|
at 550°C; | |
at 550°C; |
The CAS register number of Lithium molybdate(VI) is 13568-40-6. It also can be called as Dilithium molybdate and the IUPAC name about this chemical is dilithium dioxido(dioxo)molybdenum. The molecular formula about this chemical is Li2MoO4 and the molecular weight is 173.82. It belongs to the following product categories, such as Alternative Energy; Catalysis and Inorganic Chemistry; Electrode MaterialsChemical Synthesis; Materials Science; Molybdenum and so on.
Physical properties about Lithium molybdate(VI) are: (1)#H bond acceptors: 4; (2)#H bond donors: 2; (3)Polar Surface Area: 74.6Å2; (4)H-Bond Acceptor: 4; (5)Exact Mass: 175.917074; (6)MonoIsotopic Mass: 175.917074; (7)Topological Polar Surface Area: 80.3; (8)Heavy Atom Count: 7; (9)Complexit: 62.2; (10)Covalently-Bonded Unit Count: 3.
When you are using this chemical, please be cautious about it as the following:
This chemical is irritating to eyes, respiratory system and skin. When you are using it, wear suitable protective clothing, gloves and eye/face protection. In case of contact with eyes, rinse immediately with plenty of water and seek medical advice.
You can still convert the following datas into molecular structure:
(1)SMILES: [Li+].[Li+].[O-][Mo]([O-])(=O)=O
(2)InChI: InChI=1/2Li.Mo.4O/q2*+1;;;;2*-1/r2Li.MoO4/c;;2-1(3,4)5/q2*+1;-2
(3)InChIKey: NMHMDUCCVHOJQI-FFXFYZCHAF
(4)Std. InChI: InChI=1S/2Li.Mo.4O/q2*+1;;;;2*-1
(5)Std. InChIKey: NMHMDUCCVHOJQI-UHFFFAOYSA-N
About|Contact|Cas|Product Name|Molecular|Country|Encyclopedia
Message|New Cas|MSDS|Service|Advertisement|CAS DataBase|Article Data|Manufacturers | Chemical Catalog
©2008 LookChem.com,License: ICP
NO.:Zhejiang16009103
complaints:service@lookchem.com Desktop View