Conditions | Yield |
---|---|
With 10H-phenothiazine; hydroquinone at 110 - 130℃; for 4.5h; Temperature; | 95.7% |
With 10H-phenothiazine at 254℃; under 20252 Torr; for 0.0119444h; Microwave Irradiation; Autoclave; Industry scale; | 93% |
With hydroquinone In cyclohexane at 60 - 140℃; for 6h; |
Conditions | Yield |
---|---|
With dmap In dichloromethane Reflux; | 95% |
Conditions | Yield |
---|---|
With acid |
Conditions | Yield |
---|---|
With hydrogenchloride; tetracarbonyl nickel; benzene |
Conditions | Yield |
---|---|
With hydrogenchloride; tetracarbonyl nickel; acetone |
Conditions | Yield |
---|---|
In 1,4-dioxane; water at 50℃; for 5h; | 98% |
Conditions | Yield |
---|---|
With palladium(II) trifluoroacetate; N,N'-bis(2,6-dimethylphenyl)butane-2,3-diimine; toluene-4-sulfonic acid; p-benzoquinone In tetrahydrofuran at 20℃; under 3000.3 Torr; for 67h; Autoclave; | 92% |
Conditions | Yield |
---|---|
In ethanol at 75℃; for 15h; Michael Addition; | 89.7% |
Conditions | Yield |
---|---|
at 25 - 40℃; for 72h; | 87% |
Conditions | Yield |
---|---|
With dipotassium peroxodisulfate; palladium diacetate In trifluoroacetic acid; trifluoroacetic anhydride at 90℃; for 3h; regioselective reaction; | 75% |
octadecylacrylate
8-mesityl-4,4-difluoro-4-bora-3a,4a-diaza-s-indacene
Conditions | Yield |
---|---|
With silver(I) acetate; palladium diacetate at 80℃; for 10h; regioselective reaction; | 70% |
2,3,6-tribromo-1-methyl-1H-indole
octadecylacrylate
(2E,2'E,2''E)-trioctadecyl 3,3',3''-(1-methyl-1H-indole-2,3,6-triyl)triacrylate
Conditions | Yield |
---|---|
With dicyclohexyl-(2',6'-dimethoxybiphenyl-2-yl)-phosphane; palladium diacetate; triethylamine In N,N-dimethyl-formamide at 90℃; for 36h; Heck reaction; Inert atmosphere; | 64% |
Conditions | Yield |
---|---|
With potassium acetate; palladium diacetate; silver carbonate; Trimethylacetic acid In 1,4-dioxane at 100℃; for 24h; Sealed tube; regioselective reaction; | 62% |
Conditions | Yield |
---|---|
With samarium; copper(l) iodide; potassium iodide In tetrahydrofuran at 20℃; Molecular sieve; diastereoselective reaction; | 61% |
Conditions | Yield |
---|---|
With acetic acid In dimethyl sulfoxide at 120℃; for 40h; Sealed tube; regioselective reaction; | 53% |
octadecylacrylate
8-mesityl-4,4-difluoro-4-bora-3a,4a-diaza-s-indacene
Conditions | Yield |
---|---|
With palladium diacetate; silver trifluoroacetate at 80℃; for 24h; regioselective reaction; | 50% |
Conditions | Yield |
---|---|
With indium tris(trifluoroacetylacetonate); trimethylsilyl bromide In 1,2-dichloro-ethane at 0 - 20℃; for 2h; Inert atmosphere; | 13% |
Conditions | Yield |
---|---|
With 2,2'-azobis(isobutyronitrile) In 1,4-dioxane at 65℃; for 5h; Polymerization; |
Conditions | Yield |
---|---|
With 2,2'-azobis(isobutyronitrile) In 1,4-dioxane at 65℃; for 5h; Polymerization; |
Conditions | Yield |
---|---|
With Methyl 2-bromopropionate; copper(I) bromide; 4,4'-di-(5-nonyl)-2,2'-bipyridine; copper(ll) bromide In o-xylene at 100℃; for 10h; |
Conditions | Yield |
---|---|
With ethyl 2-bromoisobutyrate; copper(I) bromide; 4,4'-di-(5-nonyl)-2,2'-bipyridine; copper(ll) bromide In o-xylene at 100℃; for 20h; |
octadecylacrylate
Conditions | Yield |
---|---|
With copper(I) bromide; copper(ll) bromide; 4,4'-di-(5-nonyl)-2,2'-bipyridine In o-xylene at 100℃; for 20h; |
octadecylacrylate
Conditions | Yield |
---|---|
With Methyl 2-bromopropionate; copper(I) bromide; 4,4'-di-(5-nonyl)-2,2'-bipyridine; copper(ll) bromide In o-xylene at 90℃; for 30h; |
octadecylacrylate
3-(trimethoxysilyl)-1-propanethiol
polymer, radical telomerization, polymerization degree: 25; monomer(s): (3-mercaptopropyl)trimethoxysilane, 1 molar part; octadecyl acrylate, 30 molar parts
Conditions | Yield |
---|---|
With azobisisobutyronitrile In ethanol at 80℃; for 6h; |
octadecylacrylate
Conditions | Yield |
---|---|
With 2,2'-azobis(isobutyronitrile) In benzene at 59.85℃; |
styrene
poly(methacrylic acid)
octadecylacrylate
2,3-Epoxypropyl methacrylate
Polymer, Mw=8750 (GPC), Tg=66.15 deg C, radical solution copolymerization of methacrylic acid, glycidyl methacrylate, styrene and octadecyl acrylate, with a total content of 15:20:45:20 wt/wt percent, respectively
Conditions | Yield |
---|---|
With 2,2'-azobis-(2,4-dimethylvaleronitrile) In various solvent(s) at 70℃; for 8h; |
octadecylacrylate
Conditions | Yield |
---|---|
With 2,5-dimethyl-2,5-di(2-ethyl hexanoyl peroxy)-hexane In cyclohexane at 80℃; |
4-amino-3-tert-butyl-5-methylbenzenethiol
octadecylacrylate
Conditions | Yield |
---|---|
With triethylamine In toluene | 8.6 g (72%) |
The Stearyl methacrylate is an organic compound with the formula C21H40O2. The IUPAC name of this chemical is octadecyl prop-2-enoate. With the CAS registry number 4813-57-4 and EINECS 225-383-3, it is also named as 2-Propenoic acid, octadecyl ester. The product's category is Functional Monomer. What's more, this chemical is used as reactive diluent and cross-linking agent in the radiation curable system. It also can be used as resin cross-linking agent and modifier of plastic and rubber. Besides, it should be sealed in the container, kept away from light and stored in the cool and dry place.
The other characteristics of Stearyl methacrylate can be summarized as: (1)ACD/LogP: 9.83; (2)# of Rule of 5 Violations: 1; (3)ACD/LogD (pH 5.5): 9.83; (4)ACD/LogD (pH 7.4): 9.83; (5)ACD/BCF (pH 5.5): 1000000; (6)ACD/BCF (pH 7.4): 1000000; (7)ACD/KOC (pH 5.5): 5278370; (8)ACD/KOC (pH 7.4): 5278370; (9)#H bond acceptors: 2; (10)#H bond donors: 0; (11)#Freely Rotating Bonds: 19; (12)Polar Surface Area: 26.3 Å2; (13)Index of Refraction: 1.452; (14)Molar Refractivity: 100.83 cm3; (15)Molar Volume: 373.7 cm3; (16)Polarizability: 39.97×10-24 cm3; (17)Surface Tension: 30.9 dyne/cm; (18)Density: 0.868 g/cm3; (19)Flash Point: 153.1 °C; (20)Enthalpy of Vaporization: 65.11 kJ/mol; (21)Boiling Point: 400.2 °C at 760 mmHg; (22)Vapour Pressure: 1.29E-06 mmHg at 25°C.
When you are using this chemical, please be cautious about it as the following:
It has risk of serious damage to the eyes. In case of contact with eyes, rinse immediately with plenty of water and seek medical advice. If you want to contact this product, you must wear eye / face protection.
People can use the following data to convert to the molecule structure.
1. SMILES:O=C(OCCCCCCCCCCCCCCCCCC)\C=C
2. InChI:InChI=1/C21H40O2/c1-3-5-6-7-8-9-10-11-12-13-14-15-16-17-18-19-20-23-21(22)4-2/h4H,2-3,5-20H2,1H3
3. InChIKey:FSAJWMJJORKPKS-UHFFFAOYAT
4. Std. InChI:InChI=1S/C21H40O2/c1-3-5-6-7-8-9-10-11-12-13-14-15-16-17-18-19-20-23-21(22)4-2/h4H,2-3,5-20H2,1H3
5. Std. InChIKey:FSAJWMJJORKPKS-UHFFFAOYSA-N
About|Contact|Cas|Product Name|Molecular|Country|Encyclopedia
Message|New Cas|MSDS|Service|Advertisement|CAS DataBase|Article Data|Manufacturers | Chemical Catalog
©2008 LookChem.com,License: ICP
NO.:Zhejiang16009103
complaints:service@lookchem.com Desktop View